In this paper, approaches for the realization of high-resolution periodic structures with gap sizes at sub-100 nm scale by two-photon polymerization (2PP) are presented. The impact of laser intensity on the feature sizes and surface quality is investigated. The influence of different photosensitive materials on the structure formation is compared. Based on the elliptical geometry character of the voxel, the authors present an idea to realize high-resolution structures with feature sizes less than 100 nm by controlling the laser focus position with respect to the glass substrate. This investigation covers structures fabricated respectively in the plane along and perpendicular to the major axis of voxel. The authors also provide a useful approach to manage the fabrication of proposed periodic structure with a periodic distance of 200 nm and a gap size of 65 nm.

Silicones are widely used in medical applications. In ophthalmology, glaucoma drainage devices are utilized if conservative therapies are not applicable or have failed. Long-term success of these devices is limited by failure to control intraocular pressure due to fibrous encapsulation. Therefore, different medical approved silicones were tested in vitro for cell adhesion, cell proliferation and viability of human Sclera (hSF) and human Tenon fibroblasts (hTF). The silicones were analysed also depending on the sample preparation according to the manufacturer’s instructions. The surface quality was characterized with environmental scanning electron microscope (ESEM) and water contact angle measurements. All silicones showed homogeneous smooth and hydrophobic surfaces. Cell adhesion was significantly reduced on all silicones compared to the negative control. Proliferation index and cell viability were not influenced much. For development of a new glaucoma drainage device, the silicones Silbione LSR 4330 and Silbione LSR 4350, in this study, with low cell counts for hTF and low proliferation indices for hSF, and silicone Silastic MDX4-4210, with low cell counts for hSF and low proliferation indices for hTF, have shown the best results in vitro. Due to the high cell adhesion shown on Silicone LSR 40, 40,026, this material is unsuitable.

The two-photon polymerization technique (2PP) uses non-linear absorption of femtosecond laser pulses to selectively polymerize photosensitive materials. 2PP has the ability to fabricate structures with a resolution from tens of micrometers down to hundreds of nanometers. Three-dimensional microstructuring by the 2PP technique provides many interesting possibilities for biomedical applications. This microstructuring technique is suitable with many biocompatible polymeric materials, such as polyethylene glycol, polylactic acid, polycaprolactone, gelatin, zirconium-based hybrids, and others. The process of fabrication does not require clean room conditions and does not use hazard chemicals or high temperatures. The most beneficial property of 2PP is that it is capable of producing especially complex three-dimensional (3-D) structures, including devices with overhangs, without using any supportive structure. The flexibility in controlling geometries and feature sizes and the possibility to fabricate structures without the addition of new material layers makes this technique particularly appealing for fabrication of 3-D scaffolds for tissue engineering.