The work is devoted to the research of the changes that occur in the subsurface layer of the workpiece during electrical discharge machining of conductive nanocomposite based on alumina with the use of a brass tool. The nanocomposite of Al₂O₃ + 30% of TiC was electroerosively machined in a water and hydrocarbon oil. The process of electrical discharge machining is accompanied by oscillations that were registered by diagnostic means. The obtained surface of the samples was researched by the means of scanning electron microscopy and X-ray photoelectron spectroscopy. The observed surface and subsurface changes provide grounding for the conclusions on the nature of processes and reactions that occur between two electrodes and nanomodification of the obtained surfaces that can be an advantage for a series of applications.

This work is devoted to researching the tool electrode behavior and wear under discharge pulses at electrical discharge machining. The experiments were conducted on the workpieces of 12Kh18N10T (AISI 321) chrome-nickel anti-corrosion steel and D16 (AA 2024) duralumin by a 0.25-mm-diameter CuZn35 brass tool in a deionized water medium. The developed diagnostic and monitoring mean based on acoustic emission registered the oscillations accompanying machining at 4–8 kHz. The obtained workpiece and non-profiled tool surfaces were investigated by optical and scanning electron microscopy. Calculated volumetric and mass removal rates showed the difference in the character of wear at roughing and finishing. It was shown that interaction between material components in anti-corrosion steel machining had an explosive character between Zn of brass and Ni of steel at a micron level and formed multiple craters of 30–100 µm. The secondary structure and topology of worn tool surfaces were caused by material sublimation, chemical interaction between material components at high heat (10,000 °C), explosive deposition of the secondary structure. Acoustic diagnostics adequately registered the character of interaction. The observed phenomena at the submicron level and microstructure of the obtained surfaces provide grounding on the nature of material interactions and electrical erosion wear fundamentals.

Autooscillatory phenomena often accompany friction and cutting processes and have many similar features for them. The paper proposes a phenomenological model, which relates the energy of...

Vibroacoustic diagnostics is one of the most widely spread methods of uninterrupted diagnostics. It is also preferable in the technological processes when there is an absence for optical controlling tools. This paper represents the assets, which are developed for vibroacoustic diagnostics of electrical discharge machining and their experimental approbation.