Experiments were carried out according to the Nordtest protocol to study the moisture buffer potential of hemp-lime walls with a range of different internal linings and surface treatments. It was observed that the moisture buffer value was ‘Excellent’ when the inner surface of hemp-lime was exposed. ‘Excellent’ moisture buffer values were also obtained for hemp-lime with lime plaster. All other assemblies demonstrated ‘Good’ moisture buffer value. Moisture buffer values of the assemblies, after application of paint on the upper surfaces, were also determined. It was observed that application of synthetic pigment based trade paint could reduce the moisture buffer performance of the assembly consisting of hemp-lime and lime-plaster from ‘Excellent’ to ‘Good’ while between 61-69% reduction of moisture buffer value was observed for the other assemblies. However, the reduced buffer values of the assemblies are still comparable with other moisture buffering building materials. It was further observed that moisture buffer performance was improved when clay based organic paint was used instead of trade paint

The paper presents the results of a laboratory investigation on the hygric properties of five hemp insulation materials commercially available in the UK. The hemp fibre content varies between 30% and 95% in the total fibre content of the insulation materials examined. The adsorption–desorption isotherm, moisture buffer value, vapour diffusion resistance factor and water absorption coefficient were determined for the insulation materials investigated. The results showed that the hygric properties of the hemp insulation materials could vary widely depending on the constituents and fibrous structure. The considerable differences noted in the hygric properties of the insulation materials examined could potentially influence their hygrothermal performance as part of a building thermal envelope

An in situ experiment on a full-scale timber frame test building was carried out to study the hygrothermal performance of wood-hemp composite insulation in timber frame wall panels with and without a vapour barrier. The heat transfer properties and the likelihood of mould growth and condensation in the panels were compared. Step changes in the internal relative humidity were performed to explore the effects of high, normal and low internal moisture loads on the wall panels. No significant difference in the average equivalent thermal transmittance (U-values) between the panels with and without a vapour barrier was observed. The average equivalent U-values of the panels were close to the U-values calculated from the manufacturers’ declared thermal conductivity values of the insulation. The likelihood of condensation was higher at the interface of the wood-hemp insulation and the oriented strand board (OSB) in the panel without a vapour barrier. In terms of the parametric assessment of the mould germination potential, the relative humidity, the temperature and the exposure conditions in the insulation-OSB interfaces of the panel without a vapour barrier were found to be more favourable to the germination of mould spores. Nonetheless, when the insulations were dismantled, no mould was visually detected

An in situ experiment in a full scale timber frame test building was carried out to compare the hygrothermal performance of Hemp and Stone Wool insulations of identical thermal conductivity. Hemp and Stone Wool insulations were installed in timber frame wall panels without vapour barrier. The comparison was made in terms of heat transfer properties, likelihood of mould growth and condensation. Step changes in internal relative humidity were performed to explore the effect of high and normal internal moisture load on the wall panels. No significant difference between the average equivalent thermal transmittance (U-values) of the panels incorporating Hemp and Stone Wool insulations was observed. The average equivalent U-values of the panels were closer to the calculated U-values of the panels based on the manufacturers’ declared thermal conductivity of Hemp and Stone Wool insulations. It was observed that the placement of heat flux sensor along the depth of the insulation had significant influence on the measured equivalent U-value of the panels during high internal moisture load. The frequency and likelihood of condensation was higher in the interface of Stone Wool and Oriented Strand Board (OSB). In terms of the parametric assessment of mould germination potential, relative humidity, temperature and exposure conditions in the insulation-OSB interfaces were found to be favourable to germination of mould spore. However, when the insulations were dismantled, no mould was visually detected