Tungsten and its alloys have a high atomic number, high melting temperature, and high thermal conductivity, which make them fairly appropriate for use in nuclear applications in an extremely harsh radioactive environment. In recent years, there has been growing research interest in using additive manufacturing techniques to produce tungsten components with complex structures. However, the critical bottleneck for tungsten engineering manufacturing is the high melting temperature and high ductile-to-brittle transition temperature. In this study, laser powder bed fusion has been studied to produce bulk pure tungsten. And finite element analysis was used to simulate the temperature and stress field during laser irradiation. The as-printed surface as well as transverse sections were observed by optical microscopy and scanning electron microscopy to quantitatively study processing defects. The simulated temperature field suggests small-sized powder is beneficial for homogenous melting and provides guidelines for the selection of laser energy density. The experimental results show that ultra-dense tungsten bulk has been successfully obtained within a volumetric energy density of 200–391 J/mm³. The obtained relative density can be as high as 99.98%. By quantitative analysis of the pores and surface cracks, the relationships of cracks and pores with laser volumetric energy density have been phenomenologically established. The results are beneficial for controlling defects and surface quality in future engineering applications of tungsten components by additive manufacturing.