Gas-induced porosity is almost inevitable in additively manufactured aluminum alloys due to the evaporation of low-melting point elements (e.g., Al, Mg, and Zn) and the encapsulation of gases (e.g., hydrogen) during the multiple-phase reaction in the melt pool. These micropores are highly unstable during post-heat treatment at elevated temperatures and greatly affect mechanical properties and service reliability. In this study, the AlSi10Mg samples prepared by LPBF were subjected to solution heat treatment at 560 °C for 0.5 and 2 h, followed by artificial aging at 160 °C, 180 °C and 200 °C, respectively. The defect tolerance of gas porosity and associated damage mechanisms in the as-built and heat treated AlSi10Mg alloy were elucidated using optical, scanning electron microscopic analysis, X-ray micro computed tomography (XCT) and room temperature tensile testing. The results showed the defect tolerance of AlSi10Mg alloy prepared by LPBF was significantly reduced by the artificial aging treatment due to the precipitation of Mg-Si phases. Fracture analysis showed that the cooperation of fine precipitates and coarsened micropores assists nucleation and propagation of microcracks sites due to stress concentration upon tensile deformation and reduces the tensile elongation at break.