The mechanical properties, antimicrobial activity, and biocompatibility of a novel antimicrobial tissue conditioner containing cetylpyridinium chloride with montmorillonite (CPC-Mont) were evaluated. To examine the mechanical properties of the novel material, hardness, consistency, and penetration tests were conducted. Antimicrobial activity against Candida albicans (C. albicans) and Staphylococcus aureus (S. aureus) was evaluated. Cell viabilities of fibroblasts and epithelial cells using eluates from materials were measured to evaluate cytotoxicity. In addition, to assess tissue response, animal experiments were conducted. The hardness test results were similar to those of other commercially available materials. The novel tissue conditioner showed good antimicrobial activity against C. albicans and S. aureus compared with other materials. This effect was sustained for a week for C. albicans. In the case of S. aureus, microbial growth was suppressed for up to 3 weeks. Cell viability of the novel material for the eluate at 1 day was significantly less than those of other material for both cells. However, the cell viability at 7 days showed no significant difference. Animal experiments demonstrated that inflammatory responses around materials were not observed on the oral mucosa as other material. Within the limitations of this in vitro and in vivo study, the results suggest that the newly developed tissue conditioner containing CPC-Mont has not only excellent antimicrobial properties, but also the same mechanical properties and biocompatibility as tissue conditioners on the market.

Phosphoric acid-etching treatment to the hydroxyapatite (HA) surface can modify the solubility calcium structure. The aim of the present study was to develop phosphate treated porous HA, and the characteristic structures and stimulation abilities of bone formation were evaluated to determine its suitability as a new type of bone graft material. Although the phosphoric acid-etching treatment did not alter the three-dimensional structure, a micrometer-scale rough surface topography was created on the porous HA surface. Compared to porous HA, the porosity of phosphate treated porous HA was slightly higher and the mechanical strength was lower. Two weeks after placement of the cylindrical porous or phosphate treated porous HA in a rabbit femur, newly formed bone was detected in both groups. At the central portion of the bone defect area, substantial bone formation was detected in the phosphate treated porous HA group, with a significantly higher bone formation ratio than detected in the porous HA group. These results indicate that phosphate treated porous HA has a superior surface topography and bone formation abilities in vivo owing to the capacity for both osteoconduction and stimulation abilities of bone formation conferred by phosphoric acid etching.

Oral bacteria cause tooth caries and periodontal disease. Much research is being conducted to prevent both major oral diseases by rendering dental materials’ antimicrobial potential. However, such antimicrobial materials are regarded as ‘combination’ products and face high hurdles for regulatory approval. We loaded inorganic montmorillonite with the antimicrobial agent cetylpyridinium chloride, referred to below as ‘CPC-Mont’. CPC-Mont particles in a 1, 3 and 5 wt% concentration were added to the considered gold-standard self-etch adhesive Clearfil SE Bond 2 (‘CSE2’; Kuraray Noritake) to render its antibacterial potential (CSE2 without CPC-Mont served as control). Besides measuring (immediate) bonding effectiveness and (aged) bond durability to dentin, the antibacterial activity against S. mutans and the polymerization-conversion rate was assessed. Immediate and aged bond strength was not affected by 1 and 3 wt% CPC-Mont addition, while 5 wt% CPC-Mont significantly lowered bond strength and bond durability. The higher the concentration of the antimicrobial material added, the stronger the antimicrobial activity. Polymerization conversion was not affected by the CPC-Mont addition in any of the three concentrations. Hence, adding 3 wt% CPC-Mont to the two-step self-etch adhesive rendered additional antimicrobial potential on top of its primary bonding function.

Implant surface topography is a key factor in achieving osseointegration. l-Threonine can be chemically and stably bonded to titanium surfaces by phosphorylation. This study investigated the degree of in vivo osseointegration of an implant with a novel o-phospho-l-threonine (p-Thr)-binding surface. MC3T3-E1 cells were seeded on the p-Thr binding surface and machined surface disks, and initial cell attachment was evaluated. p-Thr-binding and machined surface implants were tested in vivo by implantation into the femurs of three male New Zealand white rabbits, and the osseointegration was assessed by measurement of removal torque (RT) and bone-implant contact (BIC) ratio. Initial cell attachment was greater for the p-Thr-binding than for the machined surface implant group (P < 0.05). In addition, RT and BIC values were higher for the p-Thr-binding surface than for the machined surface (P < 0.05). These results indicate that our implant with a p-Thr-binding surface can achieve enhanced osseointegration.