In this study, electron beam lithography, rather than the most popular method, chemical synthesis, is used to construct periodical TiO₂ nanowires for a gas sensor with both robust and rapid performance. The effects of temperature on the sensing response and reaction time are analyzed at various operation temperatures ranging from 200 to 350 °C. At the optimized temperature of 300 °C, the proposed sensor repeatedly obtained a rise/recovery time (ΔR: 0.9 R₀ to 0.1 R₀) of 3.2/17.5 s and a corresponding sensor response (ΔR/R₀) of 21.7% at an ethanol injection mass quantity of 0.2 μg.

This paper presents the development of tactile sensors using the sol-gel process to deposit a PZT thin-film from 250 nm to 1 μm on a flexible stainless steel substrate. The PZT thin-film tactile sensor can be used to measure human pulses from several areas, including carotid, brachial, finger, ankle, radial artery, and the apical region. Flexible PZT tactile sensors can overcome the diverse topology of various human regions and sense the corresponding signals from human bodies. The measured arterial pulse waveform can be used to diagnose hypertension and cardiac failure in patients. The proposed sensors have several advantages, such as flexibility, reliability, high strain, low cost, simple fabrication, and low temperature processing. The PZT thin-film deposition process includes a pyrolysis process at 150 °C/500 °C for 10/5 min, followed by an annealing process at 650 °C for 10 min. Finally, the consistent pulse wave velocity (PWV) was demonstrated based on human pulse measurements from apical to radial, brachial to radial, and radial to ankle. It is characterized that the sensitivity of our PZT-based tactile sensor was approximately 0.798 mV/g.

In this work, deionized (DI) water dissociation was used to treat and change the contact angle of the surface of stainless steel substrates followed by the spin coating of P(VDF-TrFE) material for the fabrication of tactile sensors. The contact angle of the stainless steel surface decreased 14° at −30 V treatment; thus, the adhesion strength between the P(VDF-TrFE) thin film and the stainless steel substrate increased by 90%. Although the adhesion strength was increased at negative voltage treatment, it is observed that the crystallinity value of the P(VDF-TrFE) thin film declined to 37% at −60 V. In addition, the remanent polarization value of the P(VDF-TrFE) thin film declined from 5.6 mC/cm² to 4.61 mC/cm² for treatment voltages between −5 V and −60 V. A maximum value of approximately 1000 KV/cm of the coercive field value was obtained with the treatment at −15 V. The d33 value was approximately −10.7 pC/N for the substrate treated at 0 V and reached a minimum of −5 pC/N for treatment at −60 V. By using the P(VDF-TrFE) thin-film as the sensing material for tactile sensors, human pulse measurements were obtained from areas including the carotid, brachial, ankle, radial artery, and apical regions. In addition, the tactile sensor is suitable for monitoring the Cun, Guan, and Chi acupoints located at the radial artery region in Traditional Chinese Medicine (TCM). Waveform measurements of the Cun, Guan, and Chi acupoints are crucial because, in TCM, the various waveforms provided information regarding the health conditions of organs.

Four types of monolayer-protected gold nanoclusters (MPCs) were synthesized and characterized as active layers of vapor sensors. An interdigitated microelectrode (IDE) and quartz crystal microbalance (QCM) were used to measure the electrical resistance and mass loading changes of MPC films during vapor sorption. The vapor sensing selectivity was influenced by the ligand structure of the monolayer on the surface of gold nanoparticles. The responses of MPC-coated QCM were mainly determined according to the affinity between the vapors and surface ligands of MPCs. The responses to the resistance changes of the MPC films were due to the effectiveness of the swelling when vapor was absorbed. It was observed that resistive sensitivity to polar organics could be greatly enhanced when the MPC contained ligands that contain interior polar functional groups with exterior nonpolar groups. This finding reveals that reducing interparticle attraction by using non-polar exterior groups could increase effective swelling and therefore enhance the sensitivity of MPC-coated chemiresistors.