Nowadays, a vast number of concrete structures are approaching the end of their expected service life. The need for maintenance and repair is high due to the continued deterioration of the existing building inventory and infrastructure, resulting in a large need for concrete repair in the near future. Reinforcement corrosion is the most important deterioration mechanism, causing (i) severe concrete damage (cracking along reinforcement and the spalling of the cover concrete) and (ii) loss in steel section. Therefore, appropriate repair techniques for corrosion damage are the main focus of this review paper. With the European transition towards a circular economy and with sustainable development goals in mind, it is also important to consider the environmental impact along with the technical requirements and life cycle cost. In order to improve the sustainability of concrete structures and repairs over their life cycle, life cycle assessment (LCA) and life cycle cost analysis (LCCA) should be applied. However, more research efforts are needed in this field for further development and refinement. This literature review tries to adress this need by compiling existing knowledge and gaps in the state-of-the-art. A comprehensive literature survey about concrete repair assessment through LCA and LCCA is performed and showed a high potential for further investigation. Additionally, it was noticed that many differences are present between the studies considering LCA and/or LCCA, namely, the considered (i) structures, (ii) damage causes, (iii) repair techniques, (iv) estimated and expected life spans, (v) LCCA methods, (vi) life cycle impact assessment (LCIA) methods, etc. Therefore, due to the case specificity, mutual comparison is challenging.

This state-of-the-art review was aimed to conduct a comprehensive literature survey to summarize experiences of crumb rubber (CR) application in concrete within the last 30 years. It shows that certain gaps prevent obtaining a coherent overview of both mechanical behaviour and environmental impact of crumb rubber concrete (CRC) to object to the stereotypes which prevent to use of CR in concrete in the construction industry. Currently, four major barriers can be distinguished for a successful CR application in the concrete industry: (1) the cost of CR recycling, (2) mechanical properties reduction, (3) insufficient research about leaching criteria and ecotoxicological risks and (4) recyclability of CRC. The application of CR in concrete has certainly its advantages and in general cannot be ignored by the construction industry. CR can be applied, for example, as an alternative material to replace natural aggregates and CRC can be used as recycled concrete aggregates (RCA) in the future. A certain diversity for the CR application can be introduced in a more efficient way when surface treatment and concrete mix design optimization are properly developed for each type of CR application in concrete for possible field applications. The role of CRC should not be limited to structures that are less dependent on strength.

The scope of the paper is to report an investigation on durability of infrastructure concrete for roads and bridges by creating a size and shape-designed pore systems in concrete in order to improve it, especially in terms of freeze–thaw resistance. By means of this experimental laboratory study, an alternative for usage of air entrainment agents (AEA) in concrete infrastructures was found in the way of using superabsorbent polymer materials (SAPs). The effect of the addition of SAPs of different amounts and different types into fresh concrete mix was investigated, including: compressive strength tests, weight loss measurements, visual and microscopic inspections and scanning electron microscopy (SEM) analysis. The detrimental strength reduction effect was not observed. The freeze–thaw procedure was varied, using different types of de-icing salts and heating/cooling regimes. It can be concluded that an improvement of the freeze–thaw resistance of concrete infrastructure depends on the particle size and optimal amount of SAPs added into concrete mix. The addition of 0.26 wt % of dry SAPs into the fresh concrete reference mix led to the significant decrease of scaling up to 43% after 28 freeze–thaw cycles. Both dosage and particle size of the SAPs had a significant impact on the obtained results and the freeze–thaw resistance in this experimental laboratory study.