Dasatinib (DAS), a potent anticancer drug, has been subjected to formulation enhancements due to challenges such as significant first-pass metabolism, poor absorption, and limited oral bioavailability. To improve its release profile, DAS was embedded in a matrix of the hydrophilic polymer polyvinylpyrrolidone (PVP). Drug amorphization was induced in a planetary ball mill by solvent-free co-grinding, facilitating mechanochemical activation. This process resulted in the formation of amorphous solid dispersions (ASDs). The ASD capsules exhibited a notable enhancement in the release rate of DAS compared to capsules containing the initial drug. Given that anticancer drugs often undergo limited metabolism in the body with unchanged excretion, the ecotoxicological effect of the native form of DAS was investigated as well, considering its potential accumulation in the environment. The highest ecotoxicological effect was observed on the bacteria Vibrio fischeri, while other test organisms (bacteria Pseudomonas putida, microalgae Chlorella sp., and duckweed Lemna minor) exhibited negligible effects. The enhanced drug release not only contributes to improved oral absorption but also has the potential to reduce the proportion of DAS that enters the environment through human excretion. This comprehensive approach highlights the significance of integrating advances in drug development while considering its environmental implications.

This study investigates the fabrication of 3D-printed microfluidic devices for solid/liquid separation, focusing on additive manufacturing technologies. Stereolithography (SLA) and fused filament fabrication (FFF) were used to create microseparators with intricate designs optimized for separation efficiency. Model suspensions containing quartz sand, nano-calcium carbonate, and talc-based baby powder in water were prepared using an electric magnetic stirrer and conveyed into the microseparator via a peristaltic pump. Different flow rates were tested to evaluate their influence on the separation efficiency. The highest separation efficiency for the model systems was observed at a flow rate of 200 mL min⁻¹. This was due to the increased turbulence at higher flow rates, which hindered the secondary flow perpendicular to the primary flow direction. The particle size distribution before and after separation was analyzed using sieve and laser diffraction, and particle morphology was inspected by scanning electron microscopy. The laser diffraction analysis revealed post-separation particle size distributions, indicating that Outlet 1 (external stream) consistently captured larger particles more effectively than Outlet 2 (internal stream). This work highlights the potential of additive manufacturing to produce customized microfluidic devices, enabling rapid prototyping and fine-tuning of complex geometries, thus enhancing separation efficiency across various industrial applications.

Purpose: The purpose of this paper is to prepare stabile emulsions with 0–15% of colloidal silica and high monomer/water ratio and to investigate the influence of silica addition and surface modification on the polyacrylate properties. Design/methodology/approach: Improving the properties of the composite can be achieved by optimizing the compatibility between the phases of the composite system with improving the interactions at the matrix/filler interface. Therefore, the silica surface was modified with nonionic emulsifier octylphenol ethoxylate, cationic initiator 2,2'-azobis-(amidinopropane dihydrochloride) and 3-methacryloxypropyltrimethoxysilane and polyacrylate/silica nanocomposites were prepared via in situ emulsion polymerization. Particle size distribution, rheological properties of the emulsions and morphology, thermal properties and mechanical properties of the film prepared from the emulsions were investigated. Findings: Polyacrylate/silica systems with unmodified silica, silica modified with nonionic emulsifier and cationic initiator have micrometer, while pure PA matrix and systems with silica modified with silane have nanometer particle sizes. Addition and surface modification of the filler increased emulsion viscosity. Agglomeration of silica particles in composites was reduced with silica surface modification. Silica filler improves thermal stability and tensile strength of polyacrylate. Originality/value: This paper provides broad spectrum of information depending on filler surface modification and latex preparation via in situ emulsion polymerization and properties with high amount of filler and monomer/water ratio with the aim that prepared latex is suitable for film formation and final application.