Graphene nanoplatelets (GNP) is a newly nanomaterial with extraordinary properties. This paper investigated the effect of GNP on the addition on freeze–thaw (F–T) resistance of concrete. In this experimental study, water to cement ratio remained unchanged, a control mixture without GNP materials and the addition of GNP was ranging from 0.02% to 0.4% by weight of ordinary Portland cement was prepared. Specimens were carried out by the rapid freeze-thaw test, according to the current Chinese standard. The workability, compressive strength, visual deterioration and mass loss of concrete samples were evaluated. Scanning electron microscopy also applied in order to investigate the micromorphology inside of the concrete. The results showed that GNP concrete has a finer pore structure than ordinary concrete; moreover, the workability of GNP concrete reduced, and the compressive strength of specimens was enhanced within the appropriate range of GNP addition; in addition, GNP concrete performed better than the control concrete in the durability of concrete exposed to F-T actions. Specimens with 0.05% GNP exhibited the highest compressive property after 200 F–T cycles compared with other samples.

Climate change has been unprecedented in the past decades or even thousands of years, which has had an adverse impact on the mechanical properties of concrete structures. Many researchers have begun to study new concrete materials. Graphene nanoplatelet (GNP) is an attractive nanomaterial that can change the crystal structure of concrete and improve durability. The aim of the present study was to investigate the effect of GNP (0.05%wt) on the carbonation depth of concrete under simulated changing climate conditions (varying temperature, relative humidity, and carbon dioxide (CO₂) concentration), and compare it with ordinary concrete. When the concentration of CO₂ is variable, the carbonation depth of graphene concrete is 10% to 20% lower than that of ordinary concrete. When the temperature is lower than 33 °C, the carbonation depth of graphene concrete is less than that of the control sample; however, above 33 °C, the thermal conductivity of GNP increases the carbonation reaction rate of concrete. When the humidity is a variable, the carbonation depth of graphene concrete is less than 15% to 30% of ordinary concrete, and when the humidity is higher than 78%, the difference in the carbonation depth between the ordinary concrete and the graphene concrete decreases gradually. The overall results indicated that GNP has a favorable effect on anti-carbonation performance under changing climate conditions.

The mortar loses strength under acid rain conditions, causing cracking, weight loss and damage to the structure. This paper studies the effects of graphenene nanoplatelets(GNP) mortar under simulated acid rain conditions. A control sample without GNP and the addition of GNP were ranging from 0.2% to 0.6% by weight of ordinary Portland cement were prepared. In different corrosion days, the mechanical properties of the GNP cement mortar were measured, scanning electron microscopy also applied. Results showed that the mechanical properties of cement mortar added with graphene are improved. Compared with the control sample, the compressive strength and flexural strength of specimens containing 0.2wt% GNP are increased by 10% and 8%, respectively. Adding GNP can improve the acid resistance and durability of cement mortar.

The transfer process of chloride ion under the action of the convection-diffusion coupling was analyzed in order to predict the corrosion of reinforcement and the durability of structure more accurately. Considering the time-varying properties of diffusion coefficient and the space-time effect of the convection velocity, the differential equation for chloride ion transfer under the action of the convection-diffusion coupling was constructed. And then the chloride ion transfer model was validated by the existing experimental datum and the actual project datum. The results showed that when only diffusion was considered, the chlorine ion concentration increased with the time and decreased with the decay index of time. Under the action of the convection-diffusion coupling, at each point of coupling region, the chloride ion concentration first increased and then decreased and tended to stabilize, and the maximum appeared at the moment of convection velocity being 0; in the diffusion zone, the chloride ion concentration increased over time, and the chloride ion concentration of the same location increased with the depth of convection (in the later period), the velocity of convection (in the early period), and the chloride ion concentration of the surface.