DP980 steels were joined using fiber laser welding. The welded joint was characterized in terms of hardness distribution and tensile behavior at room temperature, 150 ℃, and 300 ℃, respectively. The fine-grained martensite in supercritical heat affected zone (HAZ) resulted in the highest hardness (428 Hv), while the tempered martensite contributed to the hardness decreasing (‒31 Hv). Both the ultimate tensile strength and yield strength of the base metal and welded joint decreased at 150 ℃, and then increased at 300 ℃ due to dynamic strain aging (DSA). The welded joint exhibited slightly higher yield strength and lower elongation at all the test temperatures compared to base metal due to the hardened fusion zone. The energy absorption reduced slightly with increasing temperature both for base metal and welded joint, and the weld posed a minor effect on the energy absorption. Deformation was one of the requirements for DSA effect. DSA enhanced the hardness of base metal (+78 Hv) and softened zone (+53 Hv). HAZ was not softened enough to become the weakest position during tensile test.