With the rapid development of engineering component with integration,high-speed and multi-parameter,traditional techniques haven't met practical needs in extreme service environment.Laser welding,a new welding technology,has been widely used.However,it would generate the drop of mechanical properties for laser welded joint due to its thermal effect.Laser shock processing(LSP) is one of the most effective methods to improve the mechanical properties of laser welded ANSI 304 stainless steel joint.In this paper,the effects of LSP on the mechanical properties of laser welded ANSI 304 stainless steel joint have been investigated.The welded joint on the front of the tensile samples is treated by LSP impacts,and the overlapping rate of the laser spot is 50%.The tensile test of the laser welded joint with and without LSP impacts is carried out,and the fracture morphology of the tensile samples is analyzed by scanning electron microscope(SEM).Compared with the yield strength of 11.70 kN,the tensile strength of 37.66 kN,the yield-to-tensile strength ratio of 0.310 7,the elongation of 25.20%,the area reduction of 32.68% and the elastic modulus of 13 063.876 MPa,the corresponding values after LSP impacts are 14.25 kN,38.74 kN,0.367 8,26.58%,42.29% and 14 754.394 MPa,respectively.Through LSP impacts,the increasing ratio of the yield strength and tensile strength are 121.79% and 102.87%,respectively;the elongation and area reduction are improved by 5.48% and 29.38%,respectively.By comparing with coarse fracture surface of the welded joint,the delamination splitting with some cracks in the sharp corner of the welded joint and asymmetric dimples,LSP can cause brighter fracture surface,and finer and more uniform dimples.Finally,the schematic illustration of dimple formation with LSP is clearly described.The proposed research ensures that the LSP technology can clearly improve the yield strength,tensile strength,yield-to-tensile strength ratio,elongation,area reduction and elastic modulus of the welded joint.The enhancement mechanism of LSP on laser welded ANSI 304 stainless steel joint is mainly due to the fact that the refined and uniform dimples effectively delay the fracture of laser welded joints.

Tensile property was one important index of mechanical properties of ANSI 304 stainless steel laser weldments subjected to cavitation erosion (CE). Laser shock processing (LSP) was utilized to strengthen the CE resistance, and the tensile property and fracture morphology were analyzed through three replicated experiment times. Results showed tensile process of treated weldments was composed of elastic deformation, plastic deformation, and fracture. The elastic limit, elastic modulus, elongation, area reduction, and ultimate tensile strength of tensile sample after CE were higher in view of LSP. In the fracture surface, the fiber zone, radiation zone and shear lip zone were generated, and those were more obvious through LSP. The number and size of pores in the fracture surface were smaller, and the fracture surface was smoother and more uniform. The dimples were elongated along the unified direction due to effects of LSP, and the elongated direction was in agreement with the crack propagation direction. Their distribution and shape were uniform with deeper depth. It could be reflected that the tensile property was improved by LSP and the CE resistance was also enhanced.