The alkaline activation of a carbonized graphene oxide/dextrin mixture yielded a carbon-based nanoscale material (AC-TR) with a unique highly porous structure. The BET-estimated specific surface area of the material is 3167 m²/g, which is higher than the specific surface area of a graphene layer. The material has a density of 0.34 g/cm³ and electrical resistivity of 0.25 Ω·cm and its properties were studied using the elemental analysis, transmission electron microscopy (TEM), electron diffraction (ED), X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), X-ray induced Auger electron spectroscopy (XAES), and electron energy loss spectroscopy (EELS) in the plasmon excitation range. From these data, we derive an integral understanding of the structure of this material. The concentration of sp³ carbon atoms was found to be relatively low with an absolute value that depends on the measurement method. It was shown that there is no graphite-like (002) peak in the electron and X-ray diffraction pattern. The characteristic size of a sp²-domain in the basal plane estimated from the Raman spectra was 7 nm. It was also found that plasmon peaks in the EELS spectrum of AC-TR are downshifted compared to those of graphite.

New amphiphilic VP-(di)methacrylate terpolymers of different monomer compositions and topologies have been synthesized by radical polymerization in toluene without any growth regulator of polymer chains. Their structures and properties in solid state and water solution were studied by double-detector size-exclusion chromatography; IR-, ¹H, and ¹³C NMR-spectroscopy; DLS, TEM, TG, and DSC methods. The composition of the VP-AlkMA-TEGDM monomer mixture has been established to regulate the topology of the resulting macromolecules. The studied terpolymers presented on TEM images as individual low-contrast particles and their conglomerates of various sizes with highly ordered regions; in general, they are amorphous structures. None of the terpolymers demonstrated cytotoxic effects for noncancerous Vero and tumor HeLa cells. Hydrophobic D-α-tocopherol (TP) was encapsulated in terpolymer nanoparticles (NPs), and its antioxidant activity was evaluated by ABTS (radical monocation 2,2′-azino-bis(3-ethylbenzthiazoline-6-sulfonic acid)) or DPPH (2,2′-diphenyl-1-picrylhydrazyl) methods. The reaction efficiency depends on the TP-NP type. The IC₅₀ values for the decolorization reaction of ABTS^•+ and DPPH inhibition in the presence of initial and encapsulated TP were obtained.

The terpolymers of N-vinylpyrrolidone (VP) with acrylic acid and triethylene glycol methacrylate were synthesized with more than 90% yield by radical copolymerization in ethanol from monomeric mixtures of different molar composition (98:2:2, 95:5: 2 and 98:2:5) and their monomer composition, absolute molecular masses and hydrodynamic radii in aqueous media were determined. Using the MTT test, these terpolymers were established to be low toxic for non-tumor Vero cells and HeLa tumor cells. Polymer compositions of hydrophobic dye methyl pheophorbide a (MPP) based on studied terpolymers and linear polyvinylpyrrolidone (PVP) were obtained and characterized in water solution. Quantum-chemical modeling of the MPP-copolymer structures was conducted, and the possibility of hydrogen bond formation between terpolymer units and the MPP molecule was shown. Using fluorescence microscopy, the accumulation and distribution of polymer particles in non-tumor (FetMSC) and tumor (HeLa) cells was studied, and an increase in the accumulation of MPP with both types of particles was found.

The paper considers the development of a technological scheme for preparing metal matrix nanocomposites based on the interaction between nanodiamond reinforcing particles and a chromium matrix when being heated, forming chromium carbide nanoparticles. These carbides are in situ synthesized ceramic reinforcing nanoparticles. The first stage of preparing composites is to obtain composites with the chromium matrix and nanodiamond reinforcing particles. For this purpose, mechanical alloying is used, i.e., processing in planetary mills. The size of a primary nanodiamond particle is 5 nm, but they are combined in agglomerates that are hundreds of micrometers in size. The time of processing in the planetary mill defines the crushing degree of the agglomerates. In this study, processing was carried out for 0.5 h, 2 h, and 4 h. The second stage for obtaining composites with reinforcing particles of chromium carbides is thermal processing. Explorations using the method of differential scanning calorimetry showed that reducing the size of nanodiamond reinforcing particles (by prolonging the time of processing in the planetary mill) leads to a decrease in the initial temperature of the reaction for developing carbides. The worked-out technique for obtaining composites was patented in the Russian Federation (the patent for invention 2772480).