Measurement and monitoring of pH are essential in both the industry and academia. It is therefore important to continue developing novel, low-cost pH sensors that provide increased accuracy over long periods of time. Particularly promising are sensors based on materials that show pH-dependent fluorescence intensity (FI) and lifetime (FL). Carbon dots (CDs) are emerging as promising candidates because of their low cost, ease of manufacturing, low toxicity, and negligible photobleaching. However, little has been done to quantify the FI and FL values of CDs. Here we report the characterisation of the pH-dependent FI and FL of four novel solvothermal synthesised CDs. The fifth CD is used as a reference sample and was synthesised following a published synthesis. The precursors for the CDs include disperse blue 1 dye, phloroglucinol, m-phenylenediamine (m-PD), N, and N-dimethylformamide (DMF). The average diameter size of the CDs ranges from 1.5 to 15 nm. An excitation wavelength of 452 nm with a bandwidth of 45 nm was used to quantify the fluorescence in the pH range 5–9. Three CDs show a decreasing trend in FI with pH, while two CDs show an increasing trend. None of the CDs shows strong FL dependence. The FL changes around 0.5 ± 0.2 ns across the tested pH range. We suggest that the differences in the fluorescence trends can be attributed to the precursors chosen for synthesising the CDs.

Ocean acidification has become a major climate change concern requiring continuous observation. Additionally, in the industry, pH surveillance is of great importance. Consequently, there is a pressing demand to develop robust and inexpensive pH sensors. Ratiometric fluorescence pH sensing stands out as a promising concept. The application of carbon dots in fluorescent sensing presents a compelling avenue for the advancement of pH-sensing solutions. This potential is underpinned by the affordability of carbon dots, their straightforward manufacturing process, low toxicity, and minimal susceptibility to photobleaching. Thus, investigating novel carbon dots is essential to identify optimal pH-sensitive candidates. In this study, five carbon dots were synthesized through a simple solvothermal treatment, and their fluorescence was examined as a function of pH within the range of 5–9, across an excitation range of 200–550 nm and an emission range of 250–750 nm. The resulting optical features showed that all five carbon dots exhibited pH sensitivity in both the UV and visible regions. One type of carbon dot, synthesized from m-phenylenediamine, displayed ratiometric properties at four excitation wavelengths, with the best results observed when excited in the visible spectrum at 475 nm. Indeed, these carbon dots exhibited good linearity over pH values of 6–9 in aqueous Carmody buffer solution by calculating the ratio of the green emission band at 525 nm to the orange one at 630 nm (${\mathcal{I}}_{525\mathrm{nm}}$/${\mathcal{I}}_{630\mathrm{nm}}$), demonstrating highly suitable properties for ratiometric sensing.

Biofouling is one of the key factors which limits the long-term performance of seawater sensors. Common measures to hinder biofouling include toxic paints, mechanical cleaning and UV radiation. All of these measures have various limitations. A very attractive solution would be to prevent biofilm formation by changing the surface structure of the sensor. This idea has been implemented successfully in various settings, but little work has been done on structuring optically transparent materials, which are often needed in sensor applications. In order to achieve good antibiofouling properties and efficient optical transparency, the structuring must be on the nanoscale. Here, we investigate a transparent, antibiofouling surface obtained by patterning a semihexagonal nanohole structure on borosilicate glass. The nanoholes are approximately 50 nm in diameter and 200 nm deep, and the interparticle distance is 135 nm, allowing the structure to be optically transparent. The antibiofouling properties of the surface were tested by exposing the substrates to the microalgae Phaeodactylum tricornutum for four different time intervals. This species was chosen because it is common in the Norwegian coastal waters. The tests were compared with unstructured borosilicate glass substrates. The experiments show that the nanostructured surface exhibits excellent antibiofouling properties. We attribute this effect to the relative size between the structure and the biofouling microorganism. Specifically, the small dimensions of the nanoholes, compared to the biofouling microorganism, make it more difficult for the microalgae to attach. However, lubrication of the substrates with FC-70 perfluorocarbon resulted in contamination at a rate comparable to the reference substrate, possibly due to the chemical attractiveness of the alkane chains in FC-70 for the microalgae.