Oil-well cement-based materials have inherent brittleness; therefore, they cannot be directly used to seal oil and gas wells for a long time. To improve the elasticity of oil-well cement-based composites, a flexible epoxy resin system was developed. The flexibility, TG, and SEM of the cured resin system were evaluated. At the same time, the resin was added to oil-well cement-based materials to improve its elasticity. The compressive strength and elastic modulus of resin cement stone were tested, and the microstructure was analyzed by XRD, TG, and SEM/EDS. The results showed that the structure of the cured resin is compact, the thermal decomposition temperature is 243.9 °C, and it can recover its original shape after compression. At the curing age of 28 days, the compressive strength of cement-based composites containing 30% resin decreased by 26.7%, while the elastic modulus significantly decreased by 63.2%, and the elasticity of cement-based composites was significantly improved. The formation of hydration products (e.g., calcium silicate hydrate, and calcium hydroxide) in the resin cement slurry is obviously lower than that of pure cement, which is the reason for the decrease in compressive strength. The flexible structure of polymer particles and polymer film formed by epoxy resin is distributed inside the cement stone, which significantly improves the elasticity of oil-well cement-based composites. The results of this paper are helpful for the design of elastic cement slurry systems.

The surface hydrophilicity of thermoplastic rubber (TPR) is poor, and the effect of using it directly in oil well cement is not good. TPR was modified by different silane coupling agents, and the hydrophilicity of the modified TPR was studied by Fourier-transform infrared (FT-IR) spectroscopy and dispersion stability photography. The application effect of modified TPR in oil well cement slurry was also evaluated. The fracture surface morphology of TPR cement stone was observed by macrophotography and scanning electron microscopy (SEM). The results demonstrated that the hydrophilicity of TPR particles was improved after modification with silane coupling agent 3-methacryloxypropyltrimethoxysilane (KH570), and its application effect in cement slurry was excellent. Compared with the pure cement paste, the compressive strength of the cement paste with addition of TPR modified by KH570 was reduced, but the flexural strength and impact strength of the cement paste were effectively enhanced. Moreover, the modified TPR greatly improved the deformation capacity and decreased the elastic modulus of the cement paste. The modified TPR particles formed a plastic polymer network structure in the cement stone and penetrated the cement hydration products, filling in the cement paste to form a flexible structural center. Thus, it improved the mechanical properties and reduced the brittleness of cement paste.