Conventional waterborne polyurethane (WPU) has poor water resistance and poor overall performance, which limits its application in outdoor coatings. A solution to this problem is urgently needed. The introduction of fluorine-containing groups can effectively improve the water resistance of WPU. In this study, a new fluorinated chain extender (HFBMA-HPA) synthesized by free radical copolymerization and epoxy resin (E-44) were used to co-modify WPU, and five waterborne fluorinated polyurethane (WFPU) emulsions with different fluorine contents were prepared by the self-emulsification method. The effects of HFBMA-HPA content on the emulsion particle properties, coating surface properties, mechanical properties, water resistance, thermal stability, and corrosion resistance were investigated. The results showed that the WFPU coating had excellent thermal stability, corrosion resistance, and mechanical properties. As the content of HFBMA-HPA increased from 0 wt% to 14 wt%, the water resistance of the WFPU coating gradually increased, the water contact angle (WCA) increased from 73° to 98°, the water absorption decreased from 7.847% to 3.062%, and the surface energy decreased from 32.8 mN/m to 22.6 mN/m. The coatings also showed impressive performances in the adhesion and flexibility tests in extreme conditions. This study provides a waterborne fluorinated polyurethane material with excellent comprehensive performance that has potential application value in the field of outdoor waterproof and anticorrosion coatings.

Eco-friendly waterborne coatings frequently exhibit poor corrosion resistance, high solvent content, and extended curing times, attributed to the excessive employment of hydrophilic groups and petroleum-derived polyols. In this work, aniline trimer (ACAT) and polyethylene glycol (PEG) were used as chain extenders. E-44 epoxy resin was subsequently utilized to modify the system and an aniline trimer-modified waterborne polyurethane (AT-WPU) dispersion was prepared and characterized. The chemical structure of the synthesized ACAT was characterized employing 1H NMR, ESI-MS, and FTIR spectroscopy. The structure and coating performance of the AT-WPU dispersion were investigated utilizing FTIR, particle size analysis, thermogravimetric analysis, DSC, TEM, SEM, and electrochemical corrosion testing. The results demonstrate that the aniline trimer-modified waterborne polyurethane dispersion was successfully synthesized. Additionally, the DSC analysis results and thermogravimetric graphs indicate that the glass transition temperature and thermal stability of the coatings increased with the addition of aniline trimer. As the aniline trimer content increased, the hardness and adhesion of the coatings were significantly enhanced. In the electrochemical corrosion assessment, the corrosion current density of AT-WPU-3 attained 7.245 × 10⁻⁹ A·cm⁻², and the corrosion rate was as low as 0.08 μm·Y⁻¹, indicating excellent corrosion resistance. The present study provides promising practical applications in the domain of metal material protection.