Zinc- (Zn) doped hydroxyapatite (HAp) were prepared by sol-gel method. Zinc-doped hydroxyapatite (ZnHAp) and HAp were analyzed by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The Rietveld analysis revealed that the HAp and 7ZnHAp powders obtained by sol-gel method have a monophasic hydroxyapatite structure belonging to the P6_3/m spatial group. The results obtained from the ultrasound characterization of HAp and ZnHAp are also presented in this study. The effect of zinc concentration on properties that were deduced from ultrasonic measurements are studied in the case of a significant zinc concentration (x_Zn = 0.07). From the values of the ultrasonic waves velocities were determined by the pairs of elastic coefficients of the suspensions (Young modulus E, Poisson coefficient ν), which have proven to be similar to those determined by other authors.

Antibacterial cerium-doped hydroxyapatite (Ce-HAp) layers have been researched sparingly in recent years. The Ce-HAp powder, Ca_10−xCe_x(PO₄)₆(OH₎₂ with x_Ce = 0.05, was obtained by an adapted chemical co-precipitation method at room temperature. The target was prepared using the Ce-HAp (x_Ce = 0.05) powder sintered in air at 600 °C. The coatings on the Ti substrate were generated in plasma using a radio frequency (RF) magnetron sputtering discharge in an Ar gas flow in a single run. To collect the most complete information regarding the antimicrobial activity of cerium-doped hydroxyapatite with x_Ce = 0.05, (5Ce-HAp), antimicrobial studies were carried out both on the final suspensions and on the coated surfaces. The target was tested using ultrasound measurement, transmission electron microscopy (TEM), scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), glow-discharge optical emission spectroscopy (GDOES), and X-ray photoelectron spectroscopy (XPS). The present study exhibited for the first time results of the homogeneous coatings of hydroxyapatite doped with cerium using a radio frequency magnetron sputtering technique. In addition, this study highlighted for the first time the stability of the cerium-doped hydroxyapatite gels used in the creation of the coating. Ultrasound measurements on the concentrated suspension of 5Ce-HAp showed a good stability compared to double distilled, water which was chosen as the reference fluid. Particles with spherical shape were observed by both TEM and SEM analysis. The broadening of the IR bands in the IR spectrum of the 5Ce-HAp film in comparison with the IR spectrum of the precursor target indicate the formation of interlinked bonds into the layer bulk. XPS analysis revealed that the mixture of Ce³⁺ and Ce⁴⁺ ions in the hydroxyapatite (HAp) structure of the coatings could be due to the deposition process. The surface of 5Ce-HAp coatings was homogenous with particles having a spherical shape. A uniform distribution of all the constituent elements on the surface the 5Ce-HAp layer was revealed. The antimicrobial assays proved that both 5Ce-HAp suspensions and 5Ce-HAp coatings effectively inhibited the development of colony forming units (CFU) for all the tested microbial strains. Moreover, the antimicrobial assays emphasized that the 5Ce-HAp suspensions had a biocide effect against Escherichia coli (E. coli) and Candida albicans (C. albicans) microbial strains after 72 h of incubation.

Aluminum Nitride (AlN) has been long time being regarded as highly interesting material for developing sensing applications (including biosensors and implantable sensors). AlN, due to its appealing electronic properties, is envisaged lately to serve as a multi-functional biosensing platform. Although generally exploited for its intrinsic piezoelectricity, its surface morphology and mechanical performance (elastic modulus, hardness, wear, scratch and tensile resistance to delamination, adherence to the substrate), corrosion resistance and cytocompatibility are also essential features for high performance sustainable biosensor devices. However, information about AlN suitability for such applications is rather scarce or at best scattered and incomplete. Here, we aim to deliver a comprehensive evaluation of the morpho-structural, compositional, mechanical, electrochemical and biological properties of reactive radio-frequency magnetron sputtered AlN nanostructured thin films with various degrees of c-axis texturing, deposited at a low temperature (~50 °C) on Si (100) substrates. The inter-conditionality elicited between the base pressure level attained in the reactor chamber and crystalline quality of AlN films is highlighted. The potential suitability of nanostructured AlN (in form of thin films) for the realization of various type of sensors (with emphasis on bio-sensors) is thoroughly probed, thus unveiling its advantages and limitations, as well as suggesting paths to safely exploit the remarkable prospects of this type of materials.