Using p-phenylene diamine (PPD) as a modifier and nitrogen resource, nitrogen-doping reduced graphene oxide was prepared by one-step refluxing method. The influence of PPD-GO (graphene oxide) mass ratio X on surface functional groups, layer structure, and electroconductivity of nitrogen-doping reduced grapheme oxide (NRGO-X) was investigated by Fourier Transform Infrared Spectroscopy (FT-IR), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), UV-vis absorption spectrum, and electrical measurement. The results showed that GO can be simultaneously reduced and nitrogen-doped by PPD. When PPD-GO mass ratio X ≤ 6, there existed three types of N configurations in NRGO-X, including pyridinic N, pyrrolic N, and graphitic N. However, when X > 6, the pyridinic N disappeared in a six-membered ring. Further, the reduction process of NRGO as well as the nitrogen doping level and type can be regulated by changing the mass ratio X. With the increase of X, the d-spacing of NRGO-X layers increased first and then decreased, while the electrical conductivity increased gradually.

The thermal stability of bentonite is vitally important for its application in the casting field and the layer charge of montmorillonite (Q_m) is one of its central crystal-chemical parameters. As the main component of bentonite, the influence of Q_m on montmorillonite properties and behavior needs to be considered if bentonite is to be used in high-temperature environments. The objective of the current study was to investigate the relationship between Q_m and the thermal stability of Chinese bentonite samples collected from Wuhu, Anhui Province (marked as WH); Xinyang, Henan Province (marked as XY); and Santai, Sichuan Province (marked as ST) below. The values of Q_m were obtained using the O (11) method, and the structural properties of the bentonite samples were characterized by X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), thermogravimetry-differential scanning calorimetry (TG-DSC), and field emission scanning electron microscopy (FESEM). The results showed that, in the samples investigated, Q_m was inversely related to the thermal stability of bentonite. The Q_m value (electrons per half unit cell, e/huc) was greatest for sample ST (0.725 e/huc), followed by sample XY (0.470 e/huc), and by sample WH (0.354 e/huc). The dehydroxylation temperature changed related to Q_m; the sample with the largest Q_m value was WH (701°C), followed by sample XY (684°C), and sample ST (630°C). After the samples were calcined at 600°C, sample WH had the best montmorillonite structural integrity with the greatest degree of reusability (78.21%); while the montmorillonite structures of samples XY and ST were destroyed, and their reusabilities were only 9.48 and 6.01%, respectively.