As the demand for high-performance dissimilar material joining continues to increase in fields such as aerospace, biomedical engineering, and electronics, the welding technology of dissimilar materials has become a focus of research. However, due to the differences in material properties, particularly in the welding between metals and non-metals, numerous challenges arise. The formation and quality of the weld seam are strongly influenced by laser process parameters. In this study, successful welding of high-borosilicate glass to a TC4 titanium alloy, which was treated with high-temperature oxidation, was achieved using a millisecond pulsed laser. A series of process parameter comparison experiments were designed, and the laser welding behavior of the titanium alloy and glass under different process parameters was investigated using scanning electron microscopy (SEM) and a universal testing machine as the primary analysis and testing equipment. The results revealed that changes in process parameters significantly affect the energy input and accumulation during the welding process. The maximum joint strength of 60.67 N was obtained at a laser power of 180 W, a welding speed of 3 mm/s, a defocus distance of 0 mm, and a frequency of 10 Hz. Under the action of the laser, the two materials mixed and penetrated into the molten pool, thus achieving a connection. A phase, Ti₅Si₃, was detected at the fracture site, indicating that both mechanical bonding and chemical bonding reactions occurred between the high-borosilicate glass and the TC4 titanium alloy during the laser welding process.

Hermetic glass-to-metal sealing (GMTS) technology combines metal and glass and can be used to construct vacuum tubes; electric discharge tubes; semiconductor diodes; reed switches; and pressure-tight glass-to-metal windows, optical windows, and lenses in electronics or electronic systems. The hermetic and mechanically strong seals engineered using GTMS are highly reliable, making them suitable for deployment in harsh environments and for applications requiring high performance. However, it has always been challenging to precisely and robustly join glass and metal due to the significant disparities in their properties. In this study, the laser transmission welding of borosilicate glass and aluminum alloy using a pulsed Nd:YAG laser to achieve hermetic glass–metal seals was experimentally investigated. This research focused on various processing parameters and the influence of surface conditions on bonding quality. Three different types of surfaces—a polished surface, a surface subjected to preoxidation, and a laser-modified surface—were compared. To evaluate the weld strength, shear-tensile separation forces were measured. The analysis of fracture and separation encompassed detailed examinations of the weld morphology, microstructure, and elemental composition. The results revealed that increasing the laser welding energy initially enhanced the weld strength until a saturation point was reached. Among the three different surface treatments tested, the laser surface modification of aluminum alloy yielded the highest weld strength. The maximum achieved bond force exceeded 35.38 N, demonstrating the feasibility of using cost-effective pulsed laser welding for glass-to-metal sealing. The results were significantly better than those from previous research in which aluminum alloy surfaces were pretreated using microarc oxidation.