Phthalonitrile resins (PN) are known for their incredible heat resistance and at the same time poor processability. Common curing cycle of the PN includes dozens hours of heating at temperatures up to 375 °C. This work was aimed at reducing processing time of phthalonitrile resin, and with this purpose, a novolac oligomer with hydroxyl groups fully substituted by phthalonitrile moieties was synthesized with a quantitative yield. Formation of the reaction byproducts was investigated depending on the synthesis conditions. The product was characterized by ¹H NMR and FT-IR. Curing of the resins with the addition of different amounts of novolac phenolic as curing agent (25, 50 and 75 wt.%) was studied by rheological and DSC experiments. Based on these data, a curing program was developed for the further thermosets’ investigation: hot-pressing at 220 °C and 1.7 MPa for 20 min. TGA showed the highest thermal stability of the resin with 25 wt.% of novolac (T_5% = 430 °C). The post-curing program was developed by the use of DMA with different heating rates and holding for various times at 280 or 300 °C (heating rate 0.5 °C/min). Carbon and glass fiber plastic laminates were fabricated via hot-pressing of prepregs with T_g’s above 300 °C. Microcracks were formed in the CFRP, but void-free GFRP were fabricated and demonstrated superior mechanical properties (ILSS up to 86 MPa; compressive strength up to 620 MPa; flexural strength up to 946 MPa). Finally, flammability tests showed that the composite was extinguished in less than 5 s after the flame source was removed, so the material can be classified as V-0 according to the UL94 ratings. For the first time, fast-curing phthalonitrile prepregs were presented. The hot-pressing cycle of 20 min with 150 min free-standing post-curing yielded composites with the unique properties. The combination of mechanical properties, scale-up suitable fast-processing and inflammability makes the presented materials prospective for applications in the electric vehicle industries, fast train construction and the aerospace industry.

Two types of poly(5-phenyl-2-norbornene) were synthesized via ring opening metathesis and addition polymerization. The polymers sulfonation reaction under homogeneous conditions resulted in ionomer with high sulfonation degree up to 79% (IEC 3.36 meq/g). The prepared ionomer was characterized by DSC, GPC, ¹H NMR and FT-IR. Polymers for electromechanical applications soluble in common polar organic solvents were obtained by replacing proton of sulfonic group with imidazolium and 1-methylimidazlium. Membranes were prepared using the above-mentioned polymers and 1-ethyl-3-methylimidazolium tetrafluoroborate (EMImBF4), as well as mixtures with polyvinylidene fluoride (PVDF). Mechanical, morphological, and conductive properties of the membranes were examined by tensile testing, SEM, and impedance spectroscopy, respectively. Dry and air-stable actuators with electrodes based on SWCNT were fabricated via hot-pressing. Actuators with membranes based on methylimidazolium containing ionomers outperformed classical bucky gel actuator and demonstrated high strain (up to 1.14%) and generated stress (up to 1.21 MPa) under low voltage of 2 V.

Phthalonitrile thermosets are known for their excellent mechanical, physico-chemical, and fire-retardant properties, making them attractive for aerospace and mechanical engineering applications. When producing and applying phthalonitrile-based structural parts, it is essential to consider aspects such as processability and the long-term stability of the material’s properties at high temperatures. In our previous studies, we demonstrated that resins containing phosphate-bridged bisphthalonitrile monomers are easily processable due to their low melting temperature and wide processing window. In this study, we investigated the impact of bis(3-(3,4-dicyanophenoxy)phenyl)phenyl phosphate (PPhPN) monomer content on physico-chemical and mechanical properties, thermal stability, and thermal oxidative stability. This research highlights the importance of conducting long-term thermal oxidative aging studies in addition to thermogravimetric analysis to properly assess the stability of thermosets. The findings indicate that adding less than 15% of PPhPN results in the formation of a crystalline phase, which impairs the resin’s processability. Conversely, a high PPhPN content reduces the material’s thermal oxidative stability. Therefore, based on mechanical and physico-chemical tests after thermal oxidative aging, it can be concluded that a 10–15% concentration of the phosphate-containing monomer enables easy processability of the phthalonitrile resin and provides excellent long-term thermal oxidative stability at temperatures up to 300 °C, while maintaining a flexural strength exceeding 120 MPa and an elasticity modulus of 4.3 GPa.