The mechanical behavior of titanium alloys has been mostly studied in quasi-static conditions when the strain rate does not exceed 10 s⁻¹, while the studies performed in dynamic settings specifically for Ti-based composites are limited. Such data are critical to prevent the “strength margin” approach, which is used to assure the part performance under dynamic conditions in the absence of relevant data. The purpose of this study was to obtain data on the mechanical behavior of Ti-based composites under dynamic condition. The Metal Matrix Composites (MMC) on the base of the alloy Ti-6Al-4V (wt.%) were made using Blended Elemental Powder Metallurgy with different amounts of reinforcing particles: 5, 10, and 20% of TiC or 5, 10% (vol.) of TiB. Composites were studied at high strain rate compression ~1–3 × 10³·s⁻¹ using the split Hopkinson pressure bar. Mechanical behavior was analyzed considering strain rate, phase composition, microstructure, and strain energy (SE). It is shown that for the strain rates up to 1920 s⁻¹, the strength and SE of MMC with 5% TiC are substantially higher compared to particles free alloy. The particles TiC localize the plastic deformation at the micro level, and fracturing occurs mainly by crushing particles and their aggregates. TiB MMCs have a finer grain structure and different mechanical behavior. MMC with 5 and 10% TiB do not break down at strain rates up to almost 3000 s⁻¹; and 10% MMC surpasses other materials in the SE at strain rates exceeding 2200 s⁻¹. The deformation mechanism of MMCs was evaluated.

The goal of the present work is a systematic study on an influence of a strain rate on the mechanical response and microstructure evolution of the selected titanium-based materials, i.e., commercial pure titanium, Ti-6Al-4V alloy with lamellar and globular microstructures produced via a conventional cast and wrought technology, as well as Ti-6Al-4V fabricated using blended elemental powder metallurgy (BEPM). The quasi-static and high-strain-rate compression tests using the split Hopkinson pressure bar (SHPB) technique were performed and microstructures of the specimens were characterized before and after compression testing. The strain rate effect was analyzed from the viewpoint of its influence on the stress–strain response, including the strain energy, and a microstructure of the samples after compressive loading. It was found out that the Ti-6Al-4V with a globular microstructure is characterized by high strength and high plasticity (ensuring the highest strain energy) in comparison to alloy with a lamellar microstructure, whereas Ti6-Al-4V obtained with BEPM reveals the highest plastic flow stress with good plasticity at the same time. The microstructure observations reveal that a principal difference in high-strain-rate behavior of the tested materials could be explained by the nature of the boundaries between the structural components through which plastic deformation is transmitted: α/α boundaries prevail in the globular microstructure, while α/β boundaries prevail in the lamellar microstructure. The Ti-6Al-4V alloy obtained with BEPM due to a finer microstructure has a significantly better balance of strength and plasticity as compared with conventional Ti-6Al-4V alloy with a similar type of the lamellar microstructure.