In this study, highly-efficient hydrolysis of bagasse into xylose and arabinose sugars (C5 sugars) was developed by microwave-assisted oxalic acid pretreatment under mild reaction conditions. The effects of acid and hydrolysis conditions on the C5 sugar yields were discussed. The results showed that oxalic acid performed better than hydrochloric acid and maleic acid, and was a promising alternative to sulfuric acid for xylose production at the same acid concentration. The maximum yields of xylose (95.7%) and arabinose (91.5%) were achieved via the microwave-assisted oxalic acid pretreatment (120 °C, 10 min, 0.4 mol/L, solid–liquid ratio of 1:50 g/mL), indicating that almost all xylan-type hemicelluloses were released from the cell wall and hydrolyzed into C5 sugars. After pretreatment, more than 90% of the cellulose in the residual bagasse was converted to glucose (92.2%) by enzymatic hydrolysis. This approach could realize the highly-efficient hydrolysis of xylan from bagasse into C5 sugars, which would enhance the enzyme hydrolysis of treated bagasse into glucose.

Xylan-g-/P(AA-co-AM)/Graphene oxide (GO) hydrogels were prepared and used in the removal of heavy mental ions. Acrylamide (AM), acrylic acid (AA), and xylan were used as the raw materials to prepare the hydrogels with ammonium persulfate (APS) as the initiator. The prepared hydrogels were characterized by Fourier transform infrared (FTIR), thermogravimetric analysis (TGA), and energy dispersive X-ray (EDX). Some important properties of nanocomposite hydrogels such as swelling behavior, mechanical property, and adsorption capacity were also examined as well as the regeneration of the hydrogels. The results showed that the prepared hydrogels reached the equilibrium state of swelling after 12 h, and the compressive strength of the hydrogel with 30 mg of GO could reach up to 203 kPa. Compared with traditional hydrogel, the mechanical properties of the hydrogels with GO were obviously improved. The maximum adsorption capacity of hydrogels for Pb²⁺, Cd²⁺, and Zn²⁺ could reach up to 683 mg/g, 281 mg/g, and 135 mg/g, respectively. After five cycles of adsorption and desorption, the recovery rate of the hydrogels on Pb²⁺, Cd²⁺, and Zn²⁺ was still up to 87%, 80%, and 80%, respectively—all above 80%.

In order to improve the strength of polyvinyl alcohol (PVA)/xylan composite films and endow them with ultraviolet (UV) shielding ability, TiO₂-KH550 nanoparticles was synthesized and added into the PVA/xylan matrix. The TiO₂-KH550 nanoparticle dispersed well in the 0.04% sodium hexametaphosphate (SHMP) solution under ultrasonic and stirring treatments. Investigations on the properties of the films showed that TiO₂-KH550 had the positive impact on improving the strength, moisture, and oxygen barrier properties of the composite films. The maximum tensile strength (27.3 MPa), the minimum water vapor permeability (2.75 × 10⁻¹¹ g·m⁻¹·s⁻¹·Pa⁻¹), and oxygen permeability (4.013 cm³·m⁻²·24 h⁻¹·0.1MPa⁻¹) were obtained under the addition of 1.5% TiO₂-KH550. The tensile strength of TiO₂-KH550 reinforced composite film was increased by 70% than that of the pure PVA/xylan composite film, and the water vapor and oxygen permeability were decreased by 31% and 41%, respectively. Moreover, the UV transmittance of the film at the wavelength of 400 nm was almost zero when adding ≈1.5~2.5% (weight ratio, based on the total weight of PVA and xylan) of TiO₂-KH550, which indicated the PVA/xylan composite films were endowed with an excellent UV light shielding ability.