The purpose of this study was to investigate the effects of silanized spherical silica fillers (SF) on the immediate and 24-hour marginal gaps of resin-modified glass-ionomer cement (RMGIC) in tooth cavities. In correlation with marginal gap formation in the tooth cavity, these influencing factors were also examined: marginal gap and setting shrinkage of cement in the Teflon mold, as well as the shear bond strength to tooth substrate. Moreover in correlation with caries prevention, fluoride release was examined too. In this investigation, the fillers were mixed into the RMGIC powder (Fuji II LC EM). Untreated spherical silica filler (UF)-added RMGIC was used as a comparison. When compared with the control (i.e., original RMGIC), the addition of SF significantly decreased immediate marginal gap in tooth cavities and setting shrinkage in Teflon mold up to 63% and 66% respectively. Fluoride release was significantly reduced too. Apart from these results, this study showed that addition of 5wt% SF increased the shear bond strength to human enamel and dentin.

This study investigated the effects of spherical silica fillers on the physical and mechanical properties of resin-modified glassionomer cement (RMGIC). Specimens were fabricated by mixing untreated (UF) or silanized (SF) spherical silica filler into the powder of a commercially prepared RMGIC. The original RMGIC and a preparation containing 20wt% spherical silica filler were also examined with regard to their fractured surface and fluoride release. The fillers increased the compressive strength remarkably: up to 17% in the case of SF and 9% in the case of UF. Both UF and SF increased the flexural strength by up to 17%. The addition of SF increased the DTS up to 38%, but UF decreased the DTS. The addition of SF improved the workability and the mechanical properties of the RMGIC.

The purpose of this study was to evaluate the flexural strength, flexural modulus, modulus of resilience, and water sorption of four flowable light-cured composite resins (FCRs). Results were then compared with four conventional composite resins (CCRs) and a minifilled hybrid light-cured composite resin, which served as a control. Twenty specimens were flexural tested immediately after curing, while others were stored in water at 37 degrees C for 1 month, 3 months, 6 months, or 1 year before flexural testing. The 1-year specimens were weight-measured at designated time intervals to examine water sorption. All FCRs, except Point 4 Flowable, showed higher flexural strength values than their CCR counterparts (p < 0.05, Scheffé's test). After one-year water storage, the flexural strengths and flexural moduli of FCRs increased 1.5-fold or more when compared with the immediate condition. In most cases, the moduli of resilience of FCRs were higher than those of CCRs. In conclusion, it was found that FCR and CCR with the same brand name had very different characteristics and mechanical properties.

The aim of this study was to investigate how the addition of silanized spherical silica filler (SF) would influence the formation of summed, immediate interfacial gaps in Class V tooth cavities. Resin-modified glass-ionomer cement (RMGIC) is usually used for Class V restorations. As such, the following aspects of RMGIC were examined in correlation with summed interfacial gaps in the tooth cavity: setting shrinkage of cement in the Teflon mold, as well as mechanical properties in terms of compressive strength, diametral tensile strength, and flexural strength. Spherical silica filler was added to the RMGIC powder (Fuji II LC EM). For comparison purpose, untreated spherical silica filler (UF) was added too. When compared with the control (i.e., original RMGIC mixed with manufacturer-recommended powder/ liquid ratio), the addition of SF significantly decreased the formation of summed interfacial gaps in Class V cavities in the immediate condition. In particular, addition of 10 wt% SF increased the compressive strength by 56%, while diametral tensile strength was increased by 28% and flexural strength by 26%.

By means of Weibull analysis, this study evaluated and compared the flexural strength and shear bond strength of flowable light-cured composites against those of conventional ones. Twenty specimens of each material were prepared for flexural and shear bond strength measurements. Specimens were measured after water storage at 37°C for 24 hours. Three of four flowable composites showed significantly higher flexural strength than conventional ones, with Weibull moduli ranging between 6 and 14. With the presence of a bonding agent, the shear bond strength to enamel of both types was not different significantly (p=0.28), with Weibull moduli ranging between 4 and 9. In the selection of an excellent resin composite material, results of this study showed that a high, stable Weibull modulus value could be a sound indicator.

In this study, we evaluated the effects of 10 wt% spherical silica filler (SSF) addition on 24-h compressive strength, modulus of elasticity, water uptake, and immediate setting shrinkage of conventional glass-ionomer (Fuji II and Experimental) and resin-modified glass-ionomer (Fuji II LC EM) cements. The glass-ionomer cement powders were modified by being mixed with 10 wt% SSFs with an average particle diameter of 0.3 μm. The materials were mixed to consistencies similar to the flow of Fuji II mixed with a powder-liquid ratio of 2.7∶1 (w/w). The 24-h compressive strength, modulus of elasticity, water uptake, and immediate setting shrinkage were observed and the results compared with the original materials mixed with similar flow. The addition of SSF increased the compressive strength value to 1.1 times, while the increase of moduli of elasticity was 1.10 to 1.35 times. In general, the addition of SSF decreased the 24-h water uptake to 80–90% and reduced the immediate setting shrinkage to 70–79% of the original materials. The addition of 10 wt% SSF improved the characteristics of conventional and resin-modified glass-ionomer cement.