Aluminum oxide must take a spinel form (γ‐Al₂O₃) at increased temperatures in order for extensive solid solution to form between MgAl₂O₄ and α‐Al₂O₃. The solvus line between MgAl₂O₄ and Al₂O₃ has been defined at 79.6 wt% Al₂O₃ at 1500°C, 83.0 wt% Al₂O₃ at 1600°C, and 86.5 wt% Al₂O₃ at 1700°C. A metastable region has been defined at temperatures up to 1700°C which could have significant implications for material processing and properties. Additionally, initial processing could have major implications on final chemistry.