The major problem in bone tissue engineering is the development of scaffolds which can simultaneously meet the requirements of porous structure, as well as have the ability to guide the regeneration of damaged tissue by biological fixation. Composites containing biodegradable matrix and bioactive filler are the new hope in this research field. Herein we employed a simple and facile solvent casting particulate-leaching method for producing polylactide acid/hydroxyapatite (PLA/HA) composites at room temperature. FT-IR analysis confirmed the existence of necessary functional groups associated with the PLA/HA composite, whereas energy-dispersive X-ray (EDX) spectra indicated the uniform distribution of hydroxyapatite particles in the polymer matrix. The beehive-like surface morphology of the composites revealed the presence of macropores, ranged from 300 to 400 μm, whereas the thickness of the pores was noticed to be 1–2 μm. The total porosity of the scaffolds, calculated by hydrostatic weighing, was found to be 79%. The water contact angle of pure PLA was decreased from 83.6 ± 1.91° to 62.4 ± 4.17° due to the addition of hydroxyapatite in the polymer matrix. Thus, the wettability of the polymeric biomaterial could be increased by preparing their composites with hydroxyapatite. The adhesion of multipotent mesenchymal stromal cells over the surface of PLA/HA scaffolds was 3.2 times (p = 0.03) higher than the pure PLA sample. Subcutaneous implantation in mice demonstrated a good tolerance of all tested porous scaffolds and widespread ingrowth of tissue into the implant pores. HA-containing scaffolds showed a less pronounced inflammatory response after two weeks of implantation compared to pure PLA. These observations suggest that PLA/HA composites have enormous potential for hard tissue engineering and restoring maxillofacial defects.

Two variants of recombinant human bone morphogenetic protein-2 (rhBMP-2) with additional N-terminal protein domains were obtained by expression in E. coli. The N-terminal domains were s-tag (15-a.a. oligopeptide from bovine pancreatic ribonuclease A) and lz (leucine zipper dimerization domain from yeast transcription factor GCN4). The s-tag-BMP-2 and lz-BMP-2 were purified by a procedure that excluded a long refolding stage. The resulting dimeric proteins displayed higher solubility compared to rhBMP-2 without additional protein domains. Biological activity of both proteins was demonstrated in vitro by induction of alkaline phosphatase in C2C12 cells, and the activity of s-tag-BMP-2 in vivo was shown in various experimental animal models.

Three variants of human recombinant erythropoietin (rhEPO) with additional N-terminal protein domains were obtained by synthesis in an Escherichia coli heterologous expression system. These domains included (i) maltose-binding protein (MBP), (ii) MBP with six histidine residues (6His) in N-terminal position, (iii) s-tag (15-a.a. oligopeptide derived from bovine pancreatic ribonuclease A) with N-terminal 6His. Both variants of the chimeric protein containing MBP domain were prone to aggregation under nondenaturing conditions, and further purification of EPO after the domain cleavage by enterokinase proved to be impossible. In the case of 6His-s-tag-EPO chimeric protein, the products obtained after cleavage with enterokinase were successfully separated by column chromatography, and rhEPO without additional domains was obtained. Results of MALDI-TOF mass spectrometry showed that after refolding 6His-s-tag-EPO formed a structure similar to that of one of native EPO with two disulfide bonds. Both 6His-s-tag-EPO and rhEPO without additional protein domains purified after proteolysis possessed the same biological activity in vitro in the cell culture.

The aim of this work was to compare biological activities of three variants of bacterially expressed human recombinant erythropoietin (EPO) with additional protein domains: 6His-s-tag-EPO protein...

Calcium-magnesium silicate ceramics, diopside, is a promising material for use in bone plastics, but until now the possibility of its use as a carrier of recombinant bone morphogenetic protein-2 (BMP-2) has not been studied, as well as the features of reparative osteogenesis mediated by the materials based on diopside with BMP-2. Powder of calcium-magnesium silicate ceramics was obtained by solid-state synthesis using biowaste – rice husks and egg shells – as source components. Main phase of the obtained ceramics was diopside. The obtained particles were irregularly shaped with an average size of about 2.3 μm and ~20% porosity; average pore size was about 24 nm, which allowed the material to be classified as mesoporous. Diopside powder adsorbs more than 150 μg of recombinant BMP-2 per milligram, which exceeds binding capacity of hydroxyapatite, a calcium-phosphate ceramic often used in hybrid implants, by more than 3 times. In vitro release kinetics of BMP-2 was characterized by a burst release in the first 2 days and a sustained release of approximately 0.4 to 0.5% of the loaded protein over the following 7 days. In vivo experiments were performed with a mouse model of cranial defects of critical size with implantation of a suspension of diopside powder with/without BMP-2 in hyaluronic acid incorporated into the disks of demineralized bone matrix with 73-90% volume porosity and macropore size from 50 to 650 μm. Dynamics of neoosteogenesis and bone tissue remodeling was investigated histologically at the time points of 12, 21, 48, and 63 days. Diopside particles were evenly spread in the matrix and caused minimal foreign body reaction. In the presence of BMP-2 by the day 63 significant foci of newly formed bone tissue were formed in the implant pores with bone marrow areas, moreover, large areas of demineralized bone matrix in the implant center and maternal bone at the edges were involved in the remodeling. Diopside could be considered as a promising material for introduction into hybrid implants as an effective carrier of BMP-2.