Results of a study investigating a skew rolling process for elongated axisymmetric parts are presented. Despite the fact that the skew rolling technique for producing such parts was developed and implemented in the mid-twentieth century, there are no studies on this problem. The first part of this paper presents the results of FEM modelling of skew rolling stepped axles and shafts (solid and hollow). The FEM analysis was performed using the MSC Simufact Forming software. The numerical simulation involved the determination of metal flow patterns, the analysis of thermal parameters of the material during rolling, and the prediction of cracking by the Cockcroft-Latham ductile fracture criterion. Force parameters of rolling solid and hollow parts were also determined. The aim of the FEM analysis was to determine initial design assumptions and parameters for the development of the skew rolling mill. Later on in the paper, a design solution of a CNC skew rolling mill for rolling parts based on their envelope profile is proposed. FEM strength test results of a mill stand, obtained with MSC. NASTRAN, are presented. Finally, the performance test results of the constructed rolling mill are presented. The experiments involved rolling real stepped shafts that were modelled numerically. Obtained results show that the proposed skew rolling method has considerable potential. The designed and constructed rolling mill can be used to perform the rolling process according to the proposed method, with the tool and material kinematics being controlled based on the set parameters of a workpiece envelope.

The present article reports selected results of a preliminary study of the process of skew rolling of bimetallic rods. The experiments were conducted using a numerically controlled three-roller skew rolling mill. During the tests, bimetallic rods were rolled from billets whose cores and outer sleeves (bushings) were made of different types of steel. The results demonstrate that the proposed method can be successfully used in the production of bimetallic rods. However, proper fastening of the two materials depends on the geometrical parameters of the billets, and the quality of bimetallic rods depends on the heating method used. When the rods are heated without protective atmospheres, the surface layer of the core gets decarburized and the surfaces of the materials being joined together are oxidized, which hinders the welding process and adversely affects the physical and chemical properties of such products. The results of numerical modeling indicate that the material near the surface tends to flow, which may have a negative impact on the welding process. In addition, the distribution of stress in the tool–workpiece contact zone may make welding of the materials difficult. The results reported in this paper are preliminary and constitute a prelude to a more detailed analysis of bimetallic rod rolling.

The article presents and discusses the problem of determining and characterizing the cracking limits of cross-rolled specimens. The limit values were determined in accordance with the hybrid Pater criterion. For the study, the author’s test method was used, which allows the determination of the cracking moment, formed as a result of the Mannesmann effect during the compression of specimens in the channel. In order to determine the values needed to describe the cracking criterion, it was necessary to perform laboratory tests and numerical simulations of the process of compression in the channel of discs made of EA1T steel under hot forming conditions. Experimental tests were carried out for forming processes at 950 °C, 1050 °C and 1150 °C. The tested material had a disc shape with a diameter of 40 mm and a length of 20 mm, during the pressing process the diameter of the disc was reduced to a diameter of 38 mm. The increase in forming temperature caused a significant increase in the forming path until cracking occurred. Numerical tests were carried out in the finite element calculation environment Simufact.Forming 2021. The stress and strain distributions in the specimen axis were analysed during the tests, which were then used to calculate the hybrid cracking criterion limit according to Pater. After calculations according to the Pater criterion and after statistical analysis, the cracking criterion limits were obtained.

This paper presents selected results of theoretical and experimental research into the manufacture of axisymmetric bimetallic components using three-tool skew rolling technology. In the tests, it was assumed that the outer layer would be a material intended for heat treatment. However, low-carbon steel was used for the core. Experimental investigations were carried out in an innovative CNC skew rolling mill. Tests were carried out at different technological parameters of the process. In addition, the geometric parameters of the billet and the way it was heated were analyzed in relation to the quality of the resulting weld between the two materials. The quality of the weld was assessed based on metallographic observation and on strength tests (shear method). On the other hand, theoretical studies were based on numerical modeling (FEM). The numerical analysis made it possible to determine the distribution of temperature, deformation and stress in the rolling bimetallic component. The results obtained indicated that it is possible to produce bimetallic materials from the proposed steel grades. In addition, a significant effect of the method of heating the billet in the chamber furnace on the microstructure in the joining zone and the shear strength was found. There was an increase in Rc strength of about 35% when using oxidation protection. The results indicated better strength when the billet is rolling with a smaller outer layer thickness (about 50 MPa). This was confirmed by the results obtained from the FEM analysis, which indicated higher values of plastic strain and the occurrence of higher compressive stresses in the near-surface zones of the rolled bimetallic forging, both of which facilitate the welding process. From the temperature distribution (in the range of (600–1200) °C) obtained during the rolling of the bimetal forging, it can be seen that contact with cold tools does not affect the temperature in the welding zone.

Skew rolling with three rolls is used for producing axisymmetric parts. In this method, the tools are spaced every 120° on the circumference of the workpiece. They are also set askew relative to the rolling axis. Cross sectional reduction is made effective by moving the tapered rolls closer to...