In addition to sportswear and outdoor equipment, moisture-absorbent quick-drying fabrics are also widely used in everyday clothing and home textiles. In this study, three types of weft-knitted fabrics were designed using Coolmax fiber and polypropylene fiber. The Coolmax/PP fabric exhibits good stretchability with a strain of 180.5% and achieves a high cumulative individual transfer capability of 691.6%, with a water absorption rate of 50.2%/s. The moisture conductivity gradient presented good moisture and heat conductivity in a simulated human body temperature environment using an infrared camera. Furthermore, mathematical modeling was constructed and visual simulation analysis was conducted to explore moisture–thermal transfer behavior. The simulation results closely align with experimental data, providing insights into designing flexible and wearable quick-drying fabrics for thermal management.

Designing anisotropic lignin-based particles and promoting the high-value utilization of lignin have nowadays drawn much attention from scientists. However, systematic studies addressing the self-assembly mechanisms of anisotropic lignin-based particles are scarce. In this work, an interaction including the electrostatic forces and chelating forces between lignin and Ag⁺ was regulated via carboxymethylation modification. Subsequently, the aggregation morphology of carboxymethylated lignin in a Ag⁺ solution was observed via SEM. The result showed that a large number of Ag⁺ intercalated into the lignin molecules when the grafting degree of the carboxyl groups increased from 0.17 mmol/g to 0.53 mmol/g, which caused the lignin molecules to gradually transform from disordered blocks to ordered layers. Dynamics research indicated that the adsorption process of Ag⁺ in carboxymethylated lignin conforms to the Pseudo-first-order kinetic model. The saturated adsorption amount of Ag⁺ in the carboxymethylated lignin reached 1981.7 mg/g when the grafting rate of carboxyl groups increased to 0.53 mmol/g, which then fully intercalated into lignin molecules and formed a layered structure. The thermodynamic parameters showed that the thermal adsorption process conforms to the Langmuir model, which indicates that Ag⁺ is monolayer-adsorbed and intercalated into lignin molecules. Meanwhile, the ΔH values are more than 0, which suggests that this adsorption process is a endothermic reaction and that a higher temperature is conducive to an adsorption reaction. Therefore, self-assembly of lignin in a Ag⁺ solution under 70 °C is more conducive to the formation of a nanoflower structure, which is consistent with our experimental result. Finally, pH-responsive Pickering emulsions were successfully prepared using a lignin-based nanoflowers, which demonstrated their potential as a catalytic platform in the interface catalysis field. This work offers a deeper understanding into the formation mechanism of anisotropic lignin-based nanoflowers and hopes to be helpful for designing and preparing anisotropic lignin-based particles.

Electro-conductive films with excellent flexibility and thermal behavior have great potential in the fields of wearable electronics, artificial muscle, and soft robotics. Herein, we report a super-elastic and electro-conductive composite film with a sandwich structure. The composite film was constructed by spraying Polyvinyl alcohol (PVA) polymers onto a buckled conductive carbon nanotube-polydimethylsiloxane (CNTs-PDMS) composite film. In this system, the PVA and PDMS provide water sensing and stretchability, while the coiled CNT film offers sufficient conductivity. Notably, the composite film possesses high stretchability (205%), exceptional compression sensing ability, humility sensing ability, and remarkable electrical stability under various deformations. The produced CNT composite film exhibited deformation (bending/twisting) and high electro-heating performance (108 °C) at a low driving voltage of 2 V. The developed CNT composite film, together with its exceptional sensing and electrothermal performance, provides the material with promising prospects for practical applications in wearable electronics.