Enrofloxacin can be slowly delivered through polymeric systems and the addition of oil could increase the polymeric gels hydrophobicity and help the continuous release. The present work intended to develop and characterize microstructurally (XRD and FTIR) and in vitro (swelling and antimicrobial tests) the PVA hydrogels loaded with copaiba oil and Duotrill (enrofloxacin) to treat bacterial infections, as pyelonephritis, in the veterinary field. Duotrill® and oil combined diminished the gels degree of crystallinity and it was observed interaction between phases due to a new band found only in PVA hydrogels loaded with copaiba oil and Duotrill (PVA-D-O) FTIR spectrum. The samples with oil swelled less than samples without it, where copaiba oil altered the samples’ hydrophilicity. PVA-D-O presented lower weight loss and higher gel fraction than PVA, indicating the loaded material increased the gels stability. All samples containing oil and Duotrill® inhibited S. aureus.

PVA cryogels are well established as candidate biomaterials for wound healing applications but are not themselves biodegradable or antimicrobial. Blending PVA with NaCMC (CMC) or gelatin (G) can increase the gel’s ability to swell and would introduce a degree of biodegradability. The incorporation of appropriate amounts of a natural antimicrobial/healing agents, such as honey (H), would contribute to the gels properties. The present work addresses the development and characterization of layered gels (PVA-H, PVA-CMC-H and PVA-G-H, with empty PVA, PVA-CMC, PVA-G gels presented as controls). The gels were characterized by FTIR, DSC, in vitro analysis of swelling and microbiological (S. aureus) effects. Addition of gelatin, NaCMC and honey to PVA diminished the PVA chains’ ability to pack into crystallites. Samples containing honey swelled less and presented higher weight loss/biodegradability than samples without honey. Only the honey-laden PVA-CMC and PVA-G presented activity against S. aureus.

The notch effect of semicrystalline PVDF was investigated using U- and V-notch geometries with different depths, and tensile tests were performed at 23 °C using the DIC technique and FEA. Both unnotched and notched dumbbell-shaped specimens were subjected to tensile loading with the DIC technique to obtain mechanical curves and strain maps. The experimental data were compared to a numerical model, analyzing both global mechanical curves and local strain maps around the notch region to assess the accuracy of the simulations. The results demonstrated that the geometry and depth of the notch influence the mechanical behavior of PVDF, presenting a decrease in load and displacement compared to unnotched specimens. This aspect was corroborated by strain maps, which showed the increase in the local strain around the notch tip. For FEA, the global analysis indicated a good correlation with experimental results, and the local analysis demonstrated a reasonable agreement in strain map results within 0.5 mm of the notch neighborhood. Overall, the DIC technique and FEA provided a reliable evaluation of notch behavior on the PVDF used as pressure sheaths with reasonable precision.

The aging of polymers and its effect on lifespan have been of concern for many decades. Specific applications require dedicated evaluation, and pipes are among the most severe. Standard methodologies evaluate their effect under well-behaved conditions, usually considering the specimen in fully immersed media with no pressure or temperature gradients, thereby limiting their applicability. In applications where aging occurs under extreme pressure and/or temperature gradients and in aggressive media, such as pipes, diffusion through the pipe length and thickness requires a different approach. At present, there is no standard methodology to age polymers under extreme gradient conditions, and only a few published studies exist. This study presents a mid-scale, high-gradient pipe aging test methodology that approximates the operating conditions of a pressure sheath in the flexible line, thereby promoting pressure and temperature gradients that lead to plasticizer diffusion, nub formation, and property changes. The system is flexible and can be constructed at a reasonable cost.