Duplex stainless steel (DSS) exhibits good mechanical properties and corrosion resistance, and has attracted more and more attention within the fields of both science and technology. However, the increasing levels of N and of Cr, Mo, etc., as alloying elements in DSS increase production difficulty. In particular, the N element increases the risk of Cr₂N precipitation, which can seriously deteriorate the thermal plasticity of DSS, while increasing its strength. For this reason, a low-N-content 25Cr-type DSS was designed in order to adapt additive manufacturing processes. With regard to the nano-inclusions of oxide precipitation and effective grain refinement, and considering the benefits of selective laser melting fabrication, a low-N 25Cr-type duplex stainless steel with a 0.09 wt.% N content achieved high mechanical properties, with a yield strength of 712 MPa and an elongation of 27.5%, while the V-notch impact toughness was 160 J/cm². The microstructure evolution and the reasons behind the improvement in mechanical properties will be discussed in detail.

The strength of ultra-low carbon maraging stainless steels can be significantly enhanced by precipitating nanoscale intermetallic secondary phases. Retained or reversed austenite in the steel can improve its toughness, which is key to achieving an ideal combination of strength and toughness. Ti and Al are often used as cost-effective strengthening elements in maraging stainless steels but the synergistic toughening and strengthening mechanisms of Ti and Al have not been studied. To investigate the synergistic toughening and strengthening mechanisms of Ti and Al in Co-free maraging stainless steels, this paper focuses on the microstructure and mechanical properties of three alloys: Fe-12Cr-11Ni-1.7Al-0.5Ti (Steel A), Fe-12Cr-11Ni-0.5Ti (Steel B), and Fe-12Cr-11Ni-1.7Al (Steel C). The impact of Ti and Al on the microstructure and mechanical properties was investigated using X-ray diffraction (XRD), high-resolution transmission electron microscopy (TEM), and thermodynamic simulations. The relationship between microstructure, strength, and toughness is also discussed. The results indicated that Steel A, containing both Al and Ti, exhibited the highest strength level after solution treatment at 900 °C, with an ultimate tensile strength reaching 1571 MPa after aging at 540 °C. This is attributed to the simultaneous precipitation of spherical β-NiAl and rod-shaped η-Ni₃Ti phases. Steel B, with only Ti, formed a significant amount of Ni-rich reversed austenite during aging, reducing its ultimate tensile strength to 1096 MPa. Steel C, with only Al, showed a high strength–toughness combination, which was achieved by forming dispersive nano-sized intermetallic precipitates of β-NiAl in the martensitic matrix with a slight amount of austenite. It is highlighted that Al has superior toughening and strengthening effects compared to Ti in the alloy system.

In the present work, PH13-8Mo stainless steel parts without yttrium and with yttrium (Y) were manufactured by selective laser melting (SLM). The microstructure, phase composition and grain orientation of the stainless steels parts with Y and without Y were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), electron-backscatter diffraction (EBSD), transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HRTEM). The characterization results revealed that the addition of Y clearly refined the grain size of the PH13-8Mo steel formed part, resulting in more equiaxed massive grains and in a less anisotropic microstructure. PH13-8Mo stainless steel formed parts were mainly composed of martensite and retained austenite. The addition of Y could significantly increase the content of retained austenite and also generate nano-sized precipitates containing Y. The mechanical test results showed that both strength and toughness of the shaped parts containing Y were improved synergistically. The yield strength reached 1443 MPa, the elongation was 12.2%, and the room temperature impact energy reached 124.25 J/cm². The strengthening and toughening by Y of the formed parts were mainly attributed to grain refinement, higher volume fraction of the retained austenite and the formation of nano-sized precipitates containing Y.

Duplex stainless steels are widely used in many fields due to their excellent corrosion resistance and mechanical properties. However, it is a challenge to achieve duplex microstructure and excellent properties through additive manufacturing. In this work, a 0.09% N 25Cr-type duplex stainless steel was prepared by additive manufacturing (AM) and heat treatment, and its corrosion resistance was investigated. The results show that, compared with S32750 duplex stainless steel prepared by a conventional process, the combination value of film resistance and charge transfer resistance of AM duplex stainless steel was increased by 3.2–5.5 times and the pitting potential was increased by more than 100 mV. The disappearance of residual thermal stress and the reasonable distribution of Cr and N elements in the two phases are the reasons for the improvement of the corrosion resistance of AM duplex stainless steel after heat treatment. In addition, the extremely high purity of AM duplex stainless steel with no visible inclusions resulted in a higher corrosion resistance exhibited at lower pitting-resistance-equivalent number values.