Al(1060)/Mg(AZ31)/Al(1060) multilayered composite was successfully produced using an accumulative roll bonding (ARB) process for up to four cycles at an elevated temperature (400 °C). The microstructure evolution of the composites and the bonding characteristics at the interfaces between Al and Mg layers with increasing ARB cycles were characterized through optical microscopy, field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM). It was found that the grains of Al and Mg layers were significantly refined and Al₃Mg₂ and Al₁₂ Mg₁₇ intermetallic compound layers formed at the Al/Mg bonding interfaces. The strength increased gradually and the ultimate tensile strength (UTS) reached a maximum value of about 240 MPa at the third pass. Furthermore, the strengthening mechanism of the composite was analyzed based on the fracture morphologies.

In this paper, the tribological behavior of 316L stainless steel with heterogeneous lamella structure (HLS), prepared through 85% cold rolling technology and subsequent annealing treatment (750 °C, 10 min), were conducted on a ball-on-disc tribometer under different normal loads in dry ambient air conditions. The morphologies, structures, and compositions of the raw and worn surfaces were analyzed by 3D surface profilometer, XRD, SEM, EDS and TEM. Based on this, the results showed that the HLS 316L stainless steel samples exhibited lower and more steady friction coefficients than coarse-grained samples, especially under higher loads, which can be attributed to the existence of numerous oxidative particles across sliding interfaces. However, the wear resistance of HLS 316L stainless steel sample was a little weakened compared to that of the coarse-grained sample under a normal load of 5 N. When the load increases up to 15 N, an obviously decreased wear resistance was found for the HLS of the 316L stainless steel sample, which was 50% lower than that of coarse-grained sample. This can be ascribed to the more severe oxidative and abrasive wear performance of HLS 316L stainless steel sample under dry sliding conditions.