The use of graphene in a form of discontinuous flakes in polymer composites limits the full exploitation of the unique properties of graphene, thus requiring high filler loadings for achieving- for example- satisfactory electrical and mechanical properties. Herein centimetre-scale CVD graphene/polymer nanolaminates have been produced by using an iterative ‘lift-off/float-on’ process and have been found to outperform, for the same graphene content, state-of-the-art flake-based graphene polymer composites in terms of mechanical reinforcement and electrical properties. Most importantly these thin laminate materials show a high electromagnetic interference (EMI) shielding effectiveness, reaching 60 dB for a small thickness of 33 μm, and an absolute EMI shielding effectiveness close to 3·10⁵ dB cm² g⁻¹ which is amongst the highest values for synthetic, non-metallic materials produced to date.

Achieving structural superlubricity in graphitic samples of macroscale size is particularly challenging due to difficulties in sliding large contact areas of commensurate stacking domains. Here, we show the presence of macroscale structural superlubricity between two randomly stacked graphene layers produced by both mechanical exfoliation and chemical vapour deposition. By measuring the shifts of Raman peaks under strain we estimate the values of frictional interlayer shear stress (ILSS) in the superlubricity regime (mm scale) under ambient conditions. The random incommensurate stacking, the presence of wrinkles and the mismatch in the lattice constant between two graphene layers induced by the tensile strain differential are considered responsible for the facile shearing at the macroscale. Furthermore, molecular dynamic simulations show that the stick-slip behaviour does not hold for incommensurate chiral shearing directions for which the ILSS decreases substantially, supporting the experimental observations. Our results pave the way for overcoming several limitations in achieving macroscale superlubricity using graphene.

Recent findings have brought forward the potential of carbon nano-species, especially nanotubes and graphene, to impart exceptional multifunctional potential to cement, offering simultaneous enhancement of mechanical, fracture mechanical and electrical properties. While available knowledge on the topic is still limited, there is a complete absence of direct comparisons of the potential of the nano-species to improve strength and toughness and provide multifunctionality to the mortars. The study offers a comprehensive overview of these potentials, for mortars modified with pure graphene nanoplatelets and carbon nanotubes at consistent, directly comparable, concentrations up to 1.2 wt.%. Testing included flexure under pure bending moments, axial compression, electrical resistivity measurements and fracture tests under three point bending configuration; the latter were also independently assessed by acoustic emission. Differences in documented properties and optimal concentrations associated with improved mechanical performance were directly compared and rationalized in terms of nanospecies morphology. Dramatic, statistically consistent improvements in fracture behavior, up to 10-fold of control values, were documented for specific nanofiller concentrations, indicating an excellent potential of the material system for contemporary smart construction applications. An exceptionally favorable comparison of acoustic emission and fracture energy data confirmed that the non-destructive technique can independently assess the fracture performance of mortars with exceptional precision.