The aging hardening behaviours of the cold-rolled Al–Mg–Si–Sc–Zr alloy were investigated. The microstructure, hardness and electrical conductivity (EC) of the Al–Mg–Si–Sc–Zr alloy were measured. The relationship between the microstructure and the properties of the Al–Mg–Si–Sc–Zr alloy with cold-rolling and aging processes was studied. The result shows that the addition of Sc and Zr elements significantly refines the grains of the Al–Mg–Si alloy during casting. The cold rolling promotes the Al–Sc(Zr) precipitation. The precipitate strengthening increases with increasing roll reduction. The EC of the cold rolling + aging Al–Mg–Si–Sc–Zr alloy increases with increasing rolling reductions. The combination effects of the precipitation hardening and DRX softening during the aging process lead to the similar peak hardness values of around 70 HV of the rolled Al–Mg–Si–Sc–Zr alloy with the different reductions.

A380-Yb (Ytterbium) alloy was prepared by the ultrasonic melting casting method, and effects of hot extrusion on the microstructure and wear properties of the alloy were studied. The results indicate that the addition of rare earth Yb can refine the microstructure of the matrix alloy. After hot extrusion (extrusion ratio of 22.56) of the as-cast A380-Yb alloy, the secondary phase in its microstructure was further refined and the distribution became more uniform. EBSD (electron backscatter diffraction) organizational analysis shows that the average GND (geometrically necessary dislocation) density of extruded rare earth aluminum alloy is significantly increased, by 16.5 times that of the cast matrix alloy. In addition, there are a large number of grains parallel to the orientation and orientation in the extrusion direction. The alloy undergoes dynamic recrystallization during hot extrusion, and the proportion of small-angle grain boundaries is significantly reduced. Under the same friction and wear conditions, the wear rate and average friction and wear coefficient of the extruded rare earth aluminum alloy are relatively small, reduced by 53.8% and 42.6%, respectively, compared to the cast matrix alloy. Its wear mechanism is mainly abrasive wear and slight plastic deformation. In addition, the study also found that under fixed other wear conditions, as the friction speed increases, the wear rate of the extruded rare earth aluminum alloy shows a trend of first decreasing and then increasing. However, with the increase in load, its wear rate gradually increases, and the change in wear morphology is consistent with the trend of wear rate. When the wear rate is high, the wear mechanism of the extruded aluminum alloy is mainly delamination wear and adhesive wear, and is sometimes accompanied by severe plastic deformation. When the wear rate is low, its wear mechanism is mainly abrasive wear.

FeCoNiCrAl0.8Cu0.5Si0.5 high-entropy alloys were fabricated using vacuum induction melting and laser deposition processes, followed by a comparison of the structural and mechanical properties of two distinct sample types. The as-cast FeCoNiCrAl0.8Cu0.5Si0.5 alloy is comprised of BCC1, BCC2, and Cr3Si phases, while the laser-deposited alloy primarily features BCC1 and BCC2 phases. Microstructural analysis revealed that the as-cast alloy exhibits a dendritic morphology with secondary dendritic arms and densely packed grains, and the laser-deposited alloy displays a dendritic structure without the formation of granular interdendritic regions. For mechanical properties, the as-cast FeCoNiCrAl0.8Cu0.5Si0.5 alloy demonstrated higher hardness than the as-deposited alloy, with values of 586 HV0.2 and 557 HV0.2, respectively. The wear rate for the as-cast alloy was observed at 3.5 × 10⁻⁷ mm³/Nm, with abrasive wear being the primary wear mechanism. Conversely, the as-deposited alloy had a wear rate of 9.0 × 10⁻⁷ mm³/Nm, characterized by adhesive wear. The cast alloy exhibited an icorr of 4.062 μA·cm⁻², with pitting as the form of corrosion. The laser-deposited alloy showed an icorr of 3.621 μA·cm⁻², with both pitting and intergranular corrosion observed. The laser-deposited alloy demonstrated improved corrosion resistance. The investigation of their microstructure and mechanical properties demonstrates the application potential of FeCoNiCrAl0.8Cu0.5Si0.5 alloys in scenarios requiring high hardness and enhanced wear resistance.