In this study, corncob was explored as a low-cost and abundant precursor for the preparation of activated carbon via carbonization and the KOH activation method. The alkaline/biochar ratios varied from 3:1 to 5:1, and the activation temperatures ranged from 700 to 900 °C. The characterized results reveal that the alkaline/biochar ratios and activation temperatures had a remarkable influence on the morphology and microstructure of as-prepared activated carbon (CAC_T-R). The CAC_T-R presented a porous structure with a large number of micropores and a small number of mesopores. The reasonable distribution of micropores and mesopores endows the ideal structure for ion transfer and charge storage. The optimal sample CAC_700-4 exhibited the best capacitive performance with a specific capacitance of 260 F/g at 1 A/g. Moreover, the assembled CAC_700-4//CAC_700-4 symmetric supercapacitor showed a high energy density of 14.3 Wh/kg at a power density of 250 W/kg in 6 M KOH electrolyte. It also has a capacitance retention of 95.5% after 10,000 cycles, indicating its excellent cycle stability. These results indicate that corncob-derived activated carbon provides the possible application of biomass waste in high-performance supercapacitors.

Utilizing lignin-derived activated carbon in supercapacitors has emerged as a promising approach to alleviating environmental pollution and promoting the high-value utilization of byproducts in the papermaking industry. In this study, activated carbons (LACs) were prepared using a simple one-step KOH activation approach and by employing enzymatic hydrolysis lignin (EHL). The impact of the KOH activation parameters on the microstructure and capacitive performance of the LACs was investigated by varying the KOH/EHL ratio and activation temperature. The optimized sample LAC_800-4 showed an interconnected porous structure with a high surface area of 2285 m²/g, abundant micropores, and a small number of mesopores, which makes it a suitable electrode material for supercapacitors. The sample LAC_800-4 demonstrated a high specific capacitance of 291.3 F/g in a three-electrode system. Under a symmetrical supercapacitor electrode system, the specific capacitance of the LAC_800-4 electrode reached 186.8 F/g at 0.5 A/g. After 10,000 cycles at 20 A/g, the capacitance retention rate remained at 96.1%. The symmetrical supercapacitor also demonstrated a superior energy density of 6.5 Wh/kg. This work provides valuable insights into the transformation of low-value natural biomass derivatives into environmentally friendly, high-performing supercapacitor electrode materials.

Adjustment of Authorship Order