A zeolite/polyimide composite separator with a spongy-like structure was prepared by phase inversion methods based on heat-resistant polyimide (PI) polymer matrix and ZSM-5 zeolite filler, with the aim to improve the thermal stability and electrochemical properties of corresponding batteries. The separator exhibits enhanced thermal stability and no shrinkage up to 180 °C. The introduction of a certain number of ZSM-5 zeolites endows the composite separator with enhanced wettability and electrolyte uptake, better facilitating the free transport of lithium-ion. Furthermore, the composite separator shows a high ionic conductivity of 1.04 mS cm⁻¹ at 25 °C, and a high decomposition potential of 4.7 V. Compared with the PP separator and pristine PI separator, the ZSM-5/PI composite separator based LiFePO₄/Li cells have better rate capability (133 mAh g⁻¹ at 2 C) and cycle performance (145 mAh g^-1 at 0.5 C after 50 cycles). These results demonstrate that the ZSM-5/PI composite separator is promising for high-performance and high-safety lithium-ion batteries.

To realize the desired zero-dimensional behavior of a quantum dot ensemble, the ability to fabricate quantum dots with a high packing density and a high degree of size, shape, and spacing uniformity is crucial. Here we report highly ordered InAs nanodot arrays grown by molecular-beam epitaxy on nonlithographically nanopatterned GaAs. Approximately 20 billion dots are grown in a 1cm2 area with the smallest size dispersion ever reported and forming a lateral superlattice in hexagonal dense packing form. These techniques presage a pathway to controlled growth of periodic quantum dot superstructures, which offer macroscopic spatial coherence in the interaction of quantum dots with radiation.

Commercial separators (polyolefin separators) for lithium-ion batteries still have defects such as low thermostability and inferior interface compatibility, which result in serious potential safety distress and poor electrochemical performance. Zeolite/Polyacrylonitrile (Z/PAN) composite separators have been fabricated by electrospinning a polyacrylonitrile (PAN) membrane and then dip-coating it with zeolite (ZSM-5). Different from commercial separators, the Z/PAN composite separators exhibit high electrolyte uptake, excellent ionic conductivity, and prominent thermal stability. Specifically, the Z/PAN-1.5 separator exhibits the best performance, with a high electrolyte uptake of 308.1% and an excellent ionic conductivity of 2.158 mS·cm⁻¹. The Z/PAN-1.5 separator may mechanically shrink less than 10% when held at 180 °C for 30 min, proving good thermal stability. Compared with the pristine PAN separator, the Li/separator/LiFePO₄ cells with the Z/PAN-1.5 composite separator have excellent high-rate discharge capacity (102.2 mAh·g⁻¹ at 7 C) and favorable cycling performance (144.9 mAh·g⁻¹ at 0.5 C after 100 cycles). Obviously, the Z/PAN-1.5 separator holds great promise in furthering the safety and performance of lithium-ion batteries.

The traditional commercial polyolefin separators suffer from high-temperature thermal shrinkage, low electrolyte wettability and other issues. In order to improve the overall performance of the separators, electrostatic spinning technology was applied to obtain PAN nanofiber separators with an average diameter of 320 nm. Then cellulose acetate (CA) resin and nano-hydroxyapatite (HAP) were introduced to fabricate the PAN/CA/HAP composite separators through the constant temperature hot pressing and dip-coating crafts. The composite separator has a good thermal stability, with no significant dimensional change after a constant temperature treatment of 200 °C for 35 min. The electrolyte uptake rate of the PAN/CA/HAP-1.0 composite separator reaches 281%, which exhibits an efficient ionic conductivity. At the same time, it also attains a tensile strength of 11.18 MPa, which meets the requirement for separator use. Button cells assembled from PAN/CA/HAP-1.0 composite separators have an excellent rate of performance (160.42 mAh·g⁻¹ at 0.2 C) and cycle capability (157.6 mAh·g⁻¹ after 50 cycles at 0.5 C). The results support that lithium-ion batteries assembled with PAN/CA/HAP-1.0 composite separators will exhibit higher safety stability and better electrochemical performance than that of polyolefin separators, with a very immense potential for application.

The demand for high performance lithium-ion batteries (LIBs) is increasing due to widespread use of portable devices and electric vehicles. Silicon (Si) is one of the most attractive candidate anode materials for next generation LIBs. However, the high-volume change (>300%) during lithium ion alloying/de-alloying leads to poor cycle life. When Si is used as the anode, conductive carbon is needed to provide the necessary conductivity. However, the traditional carbon coating method could not overcome the challenges of pulverization and unstable Solid Electrolyte Interphase (SEI) layer during long-term cycling. Since 2010, Si/Graphene composites have been vigorously studied in hopes of providing a material with better cycling performance. This paper reviews current progress of Si/Graphene nanocomposites in LIBs. Different fabrication methods have been studied to synthesize Si/Graphene nanocomposites with promising electrochemical performances. Graphene plays a key enabling role in Si/Graphene anodes. However, the desired properties of graphene for this application have not been systematically studied and understood. Further systematic investigation of the desired graphene properties is suggested to better control the Si/Graphene anode performance.