The high worldwide demand for amorphous precipitated silica (APS) materials, millions of tons worth billions of dollars, makes it worthwhile to further expand the techniques for synthesizing new, cheap, and environmentally friendly resources. In this research, amorphous precipitated silica was synthesized from alkaline dissolution of olivine using a mixture of NaOH and KOH and characterized; this combination resulted in better kinetics than those of the separate components. Experimental parameters (concentration of alkali, liquid/solid ratio, reaction time, and temperature) were optimized to provide maximum recovery of APS from olivine dissolution, which was then characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Brunauer–Emmett–Teller (BET) N₂ adsorption–desorption measurements, and thermogravimetric analysis (TGA). The APS possessed suitable morphology for use as an additive in polymers and in catalysis: a particle size below 10 nm, pore width of 5.59 nm, BJH adsorption cumulative pore volume of 0.96 cm³ g⁻¹, BET surface area of 670.8 m² g⁻¹, and Langmuir surface area of 859.3 m² g⁻¹. The apparent activation energy of olivine dissolution with a mixture of NaOH/KOH was 43.6 kJ mol⁻¹. The steps involved in creation of APS from olivine resulted in opportunities for carbon dioxide absorption, which could contribute to the production of valuable materials through decarbonation of exhaust gases.

The utilization of dye adsorption through metal-organic frameworks represents an eco-friendly and highly effective approach in real water treatment. Here, ultrasound assisted adsorption approach was employed for the remediation of three dyes including methylene blue (MB), malachite green (MG), and congo red (CR) from real water samples using zirconium(IV)-based adsorbent (UiO-66-NH₂). The adsorbent was characterized for structural, elemental, thermal and morphological features through XRD, XPS, FTIR, thermogravimetric analysis, SEM, BET , and Raman spectroscopy. The adsorption capacity of adsorbent to uptake the pollutants in aqueous solutions was investigated under different experimental conditions such as amount of UiO-66-NH₂ at various contact durations, temperatures, pH levels, and initial dye loading amounts. The maximum removal of dyes under optimal conditions was found to be 938, 587, and 623 mg g⁻¹ towardMB, MG, and CR, respectively. The adsorption of the studied dyes on the adsorbent surface was found to be a monolayer and endothermic process. The probable mechanism for the adsorption was chemisorption and follows pseudo-second-order kinetics. From the findings of regeneration studies, it was deduced that the adsorbent can be effectively used for three consecutive cycles without any momentous loss in its adsorption efficacy. Furthermore, UiO-66-NH₂ with ultrasound-assisted adsorption might help to safeguard the environment and to develop new strategies for sustainability of natural resources.

Ag3PO4 photocatalyst has attracted interest of the scientific community in recent times due to its reported high efficiency for water oxidation and dye degradation. However, Ag3PO4 photo-corrodes if electron accepter such as AgNO3 is not used as scavenger. Synthesis of efficient Ag3PO4 followed by a simple protocol for regeneration of the photocatalyst is therefore a prerequisite for practical application. Herein, we present a facile method for the synthesis of a highly efficient Ag3PO4, whose photocatalytic efficiency was demonstrated using 3 different organic dyes: Methylene Blue (MB), Methyl orange (MO) and Rhodamine B (RhB) organic dyes for degradation tests. Approximately, 19 % of Ag3PO4 is converted to Ag0 after 4.30 hours of continuous UV-Vis irradiation in presence of MB organic dye. We have shown that the Ag/Ag3PO4 composite can be rejuvenated by a simple chemical oxidation step after several cycles of photocatalysis tests. At an optimal pH of 6.5, a mixture of cubic, rhombic dodecahedron, nanosphere and nanocrystals morphologies of the photocatalyst was formed. H2O2 served as the chemical oxidant to re-insert the surface metallic Ag into the Ag3PO4 photocatalyst but also as the agent that can control morphology of the regenerated as-prepared photocatalyst without the need for any other morphology controlling Agent (MCA). Surprisingly, the as- regenerated Ag3PO4 was found to have higher photocatalytic reactivity than the freshly made material and superior at least 17 times in comparison with the conventional Degussa TiO2, and some of TiO2 composites tested in this work.