Despite the robustness of thermosetting coatings in various applications, prolonged exposure to acidic environments can cause gradual deterioration, leading to structural or functional damage. This study investigates composite materials comprised of cycloaliphatic epoxy resin (CER) and benzoxazine (BZ) at three different weight ratios: 50:50, 25:75, and 0:100. These composites were exposed to nitric acid, simulating acid rain, for durations ranging from 1 to 5 h. The specimens were characterized for weight change, mechanical properties (flexural strength and short beam strength), and surface properties (contact angle and contact angle hysteresis). Although minimal changes in the physical and mechanical properties of both homopolymer and copolymer composites were detected after short acid exposure (up to 5 h), surface wettability analysis via static contact angle and contact angle hysteresis revealed more pronounced deterioration. The static contact angle decreased by 24.96% and 28.32% for homopolymer BZ and copolymer BZ-CER composites, respectively. Contact angle hysteresis increased by 19.39% and 27.80% for 5 h acid-exposed homopolymer BZ and copolymer CER, respectively. This study underscores the utility of surface wettability analysis as a valuable tool for monitoring deterioration from acidic aging in polymers, particularly in BZ-CER systems used in structural and high-performance applications.

Glass fiber-reinforced polymer (GFRP) composites are widely utilized across industries, particularly in structural components exposed to hygrothermal environments characterized by elevated temperature and moisture. Such conditions can significantly degrade the mechanical properties and structural integrity of GFRP composites. Therefore, it is essential to utilize effective methods for assessing their hygrothermal aging. Traditional approaches to hygrothermal aging evaluation are hindered by several limitations, including time intensity, high costs, labor demands, and constraints on specimen size due to laboratory space. This study addresses these challenges by introducing a facile and efficient alternative that evaluates GFRP degradation under hygrothermal conditions through surface wettability analysis. Herein, a glass fiber-reinforced benzoxazine (BZ) composite was fabricated using the vacuum-assisted resin transfer molding (VARTM) method and was aged in a controlled humidity and temperature chamber for up to 5 weeks. When analyzing the wettability characteristics of the composite, notable changes in the contact angle (CA) and contact angle hysteresis (CAH) were 21.77% and 90.90%, respectively. Impact droplet dynamics further demonstrated reduced wetting length and faster droplet equilibrium times with the prolonged aging duration, indicating a progressive decline in surface characteristics. These changes correlated with reductions in flexural strength, highlighting the surface’s heightened sensitivity to environmental degradation compared with internal structural integrity. This study emphasizes the critical role of surface characterization in predicting the overall integrity of GFRP composites.