All-optical fiber magnetic field sensor based on the Gd₂O₃ nano-particles (NPs)-doped alumino-silicate glass optical fiber was developed, and its temperature and vibration dependence on the Faraday Effect were investigated. Uniformly embedded Gd₂O₃ NPs were identified to form in the core of the fiber, and the measured absorption peaks of the fiber appearing at 377 nm, 443 nm, and 551 nm were attributed to the Gd₂O₃ NPs incorporated in the fiber core. The Faraday rotation angle (FRA) of the linearly polarized light was measured at 650 nm with the induced magnetic field by the solenoid. The Faraday rotation angle was found to increase linearly with the magnetic field, and it was about 18.16° ± 0.048° at 0.142 Tesla (T) at temperatures of 25 °C–120 °C, by which the estimated Verdet constant was 3.19 rad/(T∙m) ± 0.01 rad/(T∙m). The variation of the FRA with time at 0.142 T and 120 °C was negligibly small (−9.78 × 10⁻⁴ °/min). The variation of the FRA under the mechanical vibration with the acceleration below 10 g and the frequency above 50 Hz was within 0.5°.

The effect of γ-ray irradiation on the surface plasmon resonance (SPR) sensing capability of refractive index (n = 1.418–1.448) of the silica glass optical fiber comprised of germano-silicate glass cladding embedded with Au nano-particles (NPs) was investigated. As the γ-ray irradiation increased from 1 h to 3 h with the dose rate of 1190 Gy/h, the morphology of the Au NPs and the SPR spectrum were found to change. The average diameter of Au NPs increased with the aspect ratio from 1 to 2, and the nano-particles became grown to the clusters. The SPR band wavelength shifted towards a longer wavelength with the increase of total dose of γ-ray irradiation regardless of the corresponding refractive indices. The SPR sensitivities (wavelength/refractive index unit, nm/RIU) also increased from 407 nm/RIU to 3553 nm/RIU, 1483 nm/RIU, and 2335 nm/RIU after the γ-ray irradiation at a total dose of 1190 Gy, 2380 Gy, and 3570 Gy, respectively.

The effect of γ-ray irradiation on surface plasmon resonance (SPR) sensing capability of refractive index (n = 1.418–1.448) of the silica glass optical fiber comprised of germano-silicate glass cladding embedded with Au nano-particles (NPs) was investigated. As the γ-ray irradiation increased from 1 hour to 3 hours with the dose rate of 1,190 Gy/h, the morphology of the Au NPs and the SPR spectrum were found to change. The average diameter of Au NPs increased with the aspect ratio from 1 to 2 and the nano-particles became grown to the clusters. The SPR peak wavelength shifted towards longer wavelength with the increase of total dose of γ-ray irradiation regardless of the corresponding refractive indices. The SPR sensitivities (wavelength/refractive index unit, nm/RIU) also increased from 407 nm/RIU to 3,553 nm/RIU, 1,483 nm/RIU, and 2,335 nm/RIU after the γ-ray irradiation at the total dose of 1,190 Gy, 2,380 Gy, and 3,570 Gy, respectively.

SPIE Digital Library Proceedings