Yoo YJ, et al. Restor Dent Endod. 2018 Nov;44:e7. https://doi.org/10.5395/rde.2019.44.e7

The objective of root canal obturation is to achieve a fluid-tight seal. Recently, GuttaFlow bioseal (GB), a root canal sealer composed of polydimethylsiloxane, gutta-percha particles, and bioactive glass ceramics, has been developed, to enhance the sealing ability of root canal filling material. The objective of this study was to assess the sealing ability of GB using a subnanoliter-scaled fluid-flow measuring device and to compare with that of AH Plus (AH). The fluid flow in root canal-filled teeth using either gutta-percha cone (GP) with AH (GAR; n = 10) or GP with GB (GBR; n = 10) and in GP inserted in AH blocks (GA; n = 10) or GP inserted in GB blocks (GB; n = 10) was measured. In addition, fluid flow in sealer blocks of AH (A; n = 10) and GB (B; n = 10), which served as negative controls, was measured. Root canal-filled teeth using GP without any sealer (GR) acted as positive controls (n = 10). The leakage was obtained by calculating the volume of moved water by time (s), after stabilization of the fluid flow was achieved. Statistical analysis was performed using the Kruskal–Wallis test and Mann–Whitney U-test with Bonferroni correction. A p value less than 0.00238 (0.05/21) was considered significantly different. The mean leakages (nL/s) in the groups are as follows: GAR, 0.0958 ± 0.0543; GBR, 0.0223 ± 0.0246; GA, 0.0644 ± 0.0803; GB, 0.0267 ± 0.0182; A, 0.0055 ± 0.0057; B, 0.0052 ± 0.005; and GR, 0.2892 ± 0.3018. The mean leakage in the GBR group was lower than that in the GAR group (p = 0.001), while the mean leakages in the GA and GB groups were not significantly different. GuttaFlow bioseal can be useful in single-cone obturation technique.

This study investigated the influences of acidity, ethanol, and pigment on the optical properties, microhardness, and surface roughness (R_a) of a nanohybrid dental composite resin. A total of 108 disc-shaped specimens were fabricated using a nanohybrid dental composite and allocated into 36 different storage solutions according to the levels of pH (2.0, 3.0, 4.0, and 5.5), ethanol (0%, 20%, and 40%), and anthocyanin pigment (0%, 2.5%, and 12.5%). Measurements of the colorimetric parameter and the amount of color change (ΔE), translucency parameter (TP), microhardness, and surface roughness (R_a) were performed at 24 h (baseline), 1-, 2-, 3-, and 4-weeks. Repeated measures of analysis of variance (ANOVA) with a Tukey honestly significant difference test and Pearson correlation analysis were carried out (α = 0.05). Pigment of 12.5% or 40% ethanol significantly increased the ΔE (P < 0.001, P = 0.048, respectively). Pigment of 2.5% or 12.5% significantly decreased the TP (P = 0.001, P < 0.001, respectively). Microhardness of composite resin stored in pH 2.0, 3.0, 4.0 solution was lower than that for pH 5.5 (P < 0.001). Pigment, ethanol, and pH did not influence the R_a. TP change and ΔE, and R_a and ΔE had a significant positive correlation (P < 0.05). In conclusion, pigment and ethanol levels influenced the optical properties and acidity affected the microhardness of composite resin.

Oh S, et al. Restor Dent Endod. 2016 Feb;41(1):12-21. https://doi.org/10.5395/rde.2016.41.1.12

Oh S, et al. J Periodontal Implant Sci. 2019 Apr;49(2):90-104. https://doi.org/10.5051/jpis.2019.49.2.90

The aim of this study was to evaluate the long term stability of shear bond strength (SBS) when 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) containing universal adhesive was used in the ceramic bracket bonding on dental zirconia. Twenty human maxillary incisors were collected. The ceramic bracket was bonded on the buccal enamel surface after the acid-etching and orthodontic primer application (Group CON). Sixty zirconia specimens were sintered, sandblasted and divided into three experimental groups; group CP—ceramic primer followed by an orthodontic primer; group U—universal adhesive; group CU—ceramic primer followed by a universal adhesive. For each specimen, the bracket was bonded onto the treated surface with composite resin (Transbond XT, 3M ESPE). The SBS tested before (CON0, CP0, U0, CU0) and after the artificial aging (CON1, CP1, U1, CU1). The data were statistically analyzed with the Kruskal–Wallis test at a significance level of 0.05. The mean SBS of CON0, CP0, U0 and CU0 were within the clinically acceptable range without significant differences. After the aging process, SBS decreased in all groups. Among the aged groups, CP1 showed the highest SBS. Based on the results, when bonding ceramic brackets to a dental zirconia surface, we can conclude that ceramic primer used with an orthodontic primer, rather than using a universal adhesive, is recommended.