Lithium recovery is imperative to accommodate the increase in lithium demand. Salt lake brine contains a large amount of lithium and is one of the most important sources of lithium metal. In this study, Li₂CO₃, MnO₂, and TiO₂ particles were mixed, and the precursor of a manganese–titanium mixed ion sieve (M-T-LIS) was prepared by a high-temperature solid-phase method. M-T-LISs were obtained by DL-malic acid pickling. The adsorption experiment results noted single-layer chemical adsorption and maximum lithium adsorption of 32.32 mg/g. From the Brunauer–Emmett–Teller and scanning electron microscopy results, the M-T-LIS provided adsorption sites after DL-malic acid pickling. In addition, X-ray photoelectron spectroscopy and Fourier transform infrared results showed the ion exchange mechanism of the M-T-LIS adsorption. From the results of the Li⁺ desorption experiment and recoverability experiment, DL-malic acid was used to desorb Li⁺ from the M-T-LIS with a desorption rate of more than 90%. During the fifth cycle, the Li⁺ adsorption capacity of the M-T-LIS was more than 20 mg/g (25.90 mg/g), and the recovery efficiency was higher than 80% (81.42%). According to the selectivity experiment, the M-T-LIS had good selectivity for Li⁺ (adsorption capacity of 25.85 mg/g in the artificial salt lake brine), which indicates its good application potential.

Boron is a naturally occurring trace chemical element. High concentrations of boron in nature can adversely affect biological systems and cause severe pollution to the ecological environment. We examined a method to effectively remove boron ions from water systems using sugarcane bagasse biochar from agricultural waste with NH₃ nanobubbles (10% NH₃ and 90% N₂). We studied the effects of the boron solution concentration, pH, and adsorption time on the adsorption of boron by the modified biochar. At the same time, the possibility of using magnesium chloride and NH₃ nanobubbles to enhance the adsorption capacity of the biochar was explored. The carbonization temperature of sugarcane bagasse was investigated using thermogravimetric analysis. It was characterized using XRD, SEM, and BET analysis. The boron adsorption results showed that, under alkaline conditions above pH 9, the adsorption capacity of the positively charged modified biochar was improved under the double-layer effect of magnesium ions and NH₃ nanobubbles, because the boron existed in the form of negatively charged borate B(OH)₄⁻ anion groups. Moreover, cations on the NH₃ nanobubble could adsorb the boron. When the NH₃ nanobubbles with boron and the modified biochar with boron could coagulate each other, the boron was removed to a significant extent. Extended DLVO theory was adopted to model the interaction between the NH₃ nanobubble and modified biochar. The boron adsorption capacity was 36 mg/g at room temperature according to a Langmuir adsorption isotherm. The adsorbed boron was investigated using FT-IR and XPS analysis. The ammonia could be removed using zeolite molecular sieves and heating. Boron in an aqueous solution can be removed via adsorption with modified biochar with NH₃ nanobubbles and MgCl₂ addition.