Slip sliding away: Many applications would benefit from ultralow friction conditions to minimize wear on the moving parts such as in hard drives or engines. On the very small scale, ultralow friction has been observed with graphite as a lubricant. Berman et al. achieved superlubricity using graphene in combination with crystalline diamond nanoparticles and diamondlike carbon (see the Perspective by Hone and Carpick). Simulations showed that sliding of the graphene patches around the tiny nanodiamond particles led to nanoscrolls with reduced contact area that slide easily against the amorphous diamondlike carbon surface. Science , this issue p. 1118 ; see also p. 1087

The large and rapidly growing family of 2D early transition metal carbides, nitrides, and carbonitrides (MXenes) raises significant interest in the materials science and chemistry of materials communities. Discovered a little more than a decade ago, MXenes have already demonstrated outstanding potential in various applications ranging from energy storage to biology and medicine. The past two years have witnessed increased experimental and theoretical efforts toward studying MXenes’ mechanical and tribological properties when used as lubricant additives, reinforcement phases in composites, or solid lubricant coatings. Although research on the understanding of the friction and wear performance of MXenes under dry and lubricated conditions is still in its early stages, it has experienced rapid growth due to the excellent mechanical properties and chemical reactivities offered by MXenes that make them adaptable to being combined with other materials, thus boosting their tribological performance. In this perspective, the most promising results in the area of MXene tribology are summarized, future important problems to be pursued further are outlined, and methodological recommendations that could be useful for experts as well as newcomers to MXenes research, in particular, to the emerging area of MXene tribology, are provided.

Stress-induced reactions at the sliding interface during relative movement are known to cause structural or chemical modifications in contacting materials. The nature of these modifications at the atomic level and formation of byproducts in an oil-free environment, however, remain poorly understood and pose uncertainties in predicting the tribological performance of the complete tribosystem. Here, we demonstrate that tribochemical reactions occur even in dry conditions when hydrogenated diamond-like carbon (H-DLC) surface is slid against two-dimensional (2D) molybdenum disulfide along with nanodiamonds in dry nitrogen atmosphere. Detailed experimental studies coupled with reactive molecular dynamics simulations reveal that at high contact pressures, diffusion of sulfur from the dissociated molybdenum disulfide led to amorphization of nanodiamond and subsequent transformation to onion-like carbon structures (OLCs). The in situ formation of OLCs at the sliding interface provide reduced contact area as well as incommensurate contact with respect to the H-DLC surface, thus enabling successful demonstration of superlubricity