The properties of short-fiber-reinforced composites depend on the fiber length of the reinforcing fibers. This fiber length is typically influenced by processing to different extents. In this work, we investigate the influence of processing, i.e., the influence of residence time achieved via different dosing points in compounding, and the fiber content on the fiber length and mechanical properties of short-carbon-fiber-reinforced polypropylene. We found that, with increasing fiber content, the fiber length decreases from 900 to 300 µm after compounding and from 500 to 250 µm after injection molding. Additionally, a decrease in residence time in the compounder leads to an increase in the fiber length of approx. 300 µm compared to the longer residence time. This is later reduced by the injection molding step, but the longer fibers are still longer in the final molded test specimen, thus resulting in a 5–10% increased tensile strength and elastic modulus as well as an some increase in impact strength. As the injection molding step showed considerable fiber length reduction (down to 250 µm), further investigations of injection molding should be undertaken to preserve fiber length better for the increased performance of these composites.

Short-fiber reinforcement is a potent approach to improving the material properties of injection-molded parts. The main consideration in such reinforced materials is to preserve the fiber length, as this is the major influence on the properties of a given composite. The aim of this work was to investigate the different influencing parameters in injection molding processing on the properties of short carbon and glass fiber-reinforced polypropylene. We investigated parameters like melt temperature and back pressure, but also machine size and pre-heating regarding their influence on the tensile properties. We found that adjustments of melt temperature and back pressure only yield small improvements in the fiber length and the tensile properties, also depending on machine size, but a pre-heating step of the granules can significantly improve the properties.

Natural fiber composites have gained increasing attention due to sustainability considerations. One often neglected aspect is the potential for the mechanical recycling of such materials. In this work, we compounded injection-molded polypropylene (PP) and polylactic acid (PLA) short cellulose fiber composites with fiber shares up to 40 percent by weight. Both matrix materials were reinforced by the addition of the fibers. We investigated a trifold full recycling process, where we subjected the materials produced in the first place to compounding, injection molding, testing, and shredding, and then repeated the process. Although the materials’ properties assigned to degradation were found to decrease with progressive recycling, attractive mechanical properties could be preserved even after the third reprocessing cycle.

Continuous-fibre-reinforced thermoplastics are attractive materials for industries to cut down on weight in structural components. Recycling these parts or trims generated during production is difficult due to the reduced properties in materials intended for high-performance applications. Our study investigates the recyclability of short-fibre-reinforced compounds made from shredded organosheets. The fibre share was varied by the addition of virgin polypropylene, and three recycling rounds via a reduced injection-moulding process and a full thermomechanical recycling process including a compounding step were compared. Organosheet cuttings were found to be able to be applied as a short-glass-fibre source for the production of composites with varying fibre shares. Up to 14,000 MPa of elastic modulus and 80 MPa of tensile strength could be achieved at a fibre content of 45 vol%. Fibre length was reduced with progressive processing, less so for lower fibre shares, and in the reduced process without the shear and stress of the compounding step. Fibres from organosheets might be present in bundles and disperse in the matrix with progressive processing, which is particularly the case without compounding processes and can also influence the mechanical properties.

Some recycled plastics would provide the mechanical, thermal, and optical properties to replace virgin materials in some applications, but they are not used bec