Neat poly(vinylidene fluoride) (PVDF) ultrafiltration (UF) membranes exhibit poor water permeance and surface hydrophobicity, resulting in poor antifouling properties. Herein, we report the synthesis of a fluorine-containing amphiphilic graft copolymer, poly(2,2,2-trifluoroethyl methacrylate)-g-poly(ethylene glycol) behenyl ether methacrylate (PTFEMA-g-PEGBEM), hereafter referred to as PTF, and its effect on the structure, morphology, and properties of PVDF membranes. The PTF graft copolymer formed a self-assembled nanostructure with a size of 7–8 nm, benefiting from its amphiphilic nature and microphase separation ability. During the nonsolvent-induced phase separation (NIPS) process, the hydrophilic PEGBEM chains were preferentially oriented towards the membrane surface, whereas the superhydrophobic PTFEMA chains were confined in the hydrophobic PVDF matrix. The PTF graft copolymer not only increased the pore size and porosity but also significantly improved the surface hydrophilicity, flux recovery ratio (FRR), and antifouling properties of the membrane. The membrane performance was optimal at 5 wt.% PTF loading, with a water permeance of 45 L m⁻² h⁻¹ bar⁻¹, a BSA rejection of 98.6%, and an FRR of 83.0%, which were much greater than those of the neat PVDF membrane. Notably, the tensile strength of the membrane reached 6.34 MPa, which indicated much better mechanical properties than those reported in the literature. These results highlight the effectiveness of surface modification via the rational design of polymer additives and the precise adjustment of the components for preparing membranes with high performance and excellent mechanical properties.

Thin-film composite (TFC) membranes containing various fillers and additives present an effective alternative to conventional dense polymer membranes, which often suffer from low permeance (flux) and the permeability–selectivity tradeoff. Alongside the development and utilization of numerous new polymers over the past few decades, diverse additives such as metal–organic frameworks (MOFs), graphene oxides (GOs), and ionic liquids (ILs) have been integrated into the polymer matrix to enhance performance. However, achieving desirable interfacial compatibility between these additives and the host polymer matrix, particularly in TFC structures, remains a significant challenge. This review discusses recent advancements in TFC membranes for CO₂/N₂ separation, focusing on material structure, polymer–additive interaction, interface and separation properties. Specifically, we examine membranes operating under dry conditions to clearly assess the impact of additives on membrane properties and performance. Additionally, we provide a perspective on future research directions for designing high-performance membrane materials.