Objectives: The objective of this study was to investigate the mechanical properties of high-impact (HI) heat-cured acrylic resin (PMMA) reinforced with silane-treated zirconia nanoparticles. Methods: Forty-five PMMA specimens reinforced with zirconia were fabricated and divided into three groups: Pure HI PMMA (control group), PMMA reinforced with 3 wt.% of non-silanised zirconia nanoparticles and PMMA reinforced with 3 wt.% of silanised zirconia nanoparticles. Silanised and non-silanised zirconia nanoparticles were analysed with Fourier Transform Infrared (FTIR) Spectroscopy. For measuring the flexural modulus and strength, a Zwick universal tester was used, and for surface hardness, a Vickers hardness tester were used. Furthermore, raw materials and fractured surfaces were analysed using Scanning Electron Microscopy (SEM). A one-way ANOVA test followed by a post-hoc Bonferroni test was employed to analyse the data. Results: The results showed that the mean values for flexural strength (83.5 ± 6.2 MPa) and surface hardness (20.1 ± 2.3 kg/mm²) of the group containing 3 wt.% treated zirconia increased significantly (p < 0.05) in comparison to the specimens in the group containing non-treated zirconia (59.9 ± 7.1 MPa; 15.0 ± 0.2 kg/mm²) and the control group (72.4 ± 8.6 MPa; 17.1 ± 0.9 kg/mm²). However, the group with silanised zirconia showed an increase in flexural modulus (2313 ± 161 MPa) but was not significantly different (p > 0.05) from the non-silanised group (2207 ± 252 MPa) and the control group (1971 ± 235 MPa). Conclusion: Silane-treated zirconia nano-filler improves the surface hardness and flexural strength of HI PMMA-zirconia nanocomposites, giving a potentially longer service life of the denture base.

Biodentine is a calcium silicate cement (CSC) that has been broadly applied in vital pulp therapy. The quality of the Biodentine-composite bond has a significant effect on the longevity of the definitive restoration. The aim of this study is to investigate the shear bond strength (SBS) between Biodentine and composite restoration at different maturation times of Biodentine aged in artificial saliva. Fifteen Biodentine discs were allocated into three groups (n = 5) based on the timeframe of performance of composite restoration: immediate (after 12 min), after 14 days, and after 28 days of Biodentine maturation. Total etch and rinse adhesive system and bulk-fill regular resin composite were used. The shear bond strength and the failure pattern were assessed. One-way ANOVA with the Bonferroni post hoc test was applied for statistical analysis at . The highest (32.47 ± 8.18 MPa) and the lowest (4.08 ± 0.81 MPa) SBS values were recorded for 14 days and 12 min groups, respectively. Significant statistical differences were reported among the groups, and a high statistically significant difference was found between the immediate group and the other groups. Adhesive failure patterns were evident in all groups. More clinically acceptable bond strength between the Biodentine and overlaid composite restoration is at 14 days after Biodentine maturation. Delaying the coverage of Biodentine later than 14 days may significantly reduce the SBS. Using the artificial saliva as an aging medium may affect the SBS between Biodentine and composite material.

Peracetic acid (PAA) is widely used as a sterilizing/disinfecting agent, and, in endodontics, it has been introduced as a promising irrigant in root canal treatment. It has been used at different concentrations to achieve various functions. However, endodontic instruments in contact with PAA of a certain concentration may affect their fatigue resistance. Therefore, the aim of this study was to investigate the impact of PAA on the cyclic fatigue resistance of three commercial heat-treated nickel-titanium (NiTi) rotary files. Three types of heat-treated NiTi rotary files were selected: One Curve (OC), ProTaper Gold (PTG), and Wave One Gold (WOG). Each type was divided into three subgroups (n = 6 for each file type): (1) untreated instruments; (2) files immersed in 0.002% PAA; and (3) files immersed in 0.35% PAA. The performance of each file type was tested in a simulated canal. The number of cycles to fracture (NCF) was determined to assess cyclic fatigue resistance of the files. Independent sample t-test was applied to compare each treated file within a subgroup with its respective control group, and one-way ANOVA was used for comparison among the main groups. All types of tested files revealed a significant decline in the cyclic fatigue resistance after exposure to 0.002% PAA except the PTG ( ). After exposure of the files to a higher concentration (0.35% PAA), a dramatic reduction was demonstrated by all the groups. Before and after exposure of the files to PAA, PTG displayed the highest cyclic fatigue resistance, followed by the WOG, while the OC showed the lowest resistance. Exposure of heated-treated NiTi files to PAA in a relatively high or low concentration adversely affects the cyclic fatigue resistance. The PTG files demonstrated the best performance among the tested types and can be disinfected with 0.002% PAA for clinical purpose.

Objective: Evaluate the effects of different storage periods on flexural strength (FS) and degree of conversion (DC) of Bis-Acryl composite and Urethane dimethacrylate provisional restorative materials. Material and Methods: A total of 60 specimens were prepared from four temporary crown materials commercially available and assigned to four tested groups (n = 15 for each group): Prevision Temp, B&E CROWN, Primma Art, and Charm Temp groups. The specimens were stored in artificial saliva, and the FS was tested after 24 h, 7 d, and 14 d. A standard three-point bending test was conducted using a universal testing machine. Additionally, the DC was determined using a Fourier transform infrared spectroscopy (FTIR) device. The data were analyzed statistically using twoway ANOVA, Tukey`s HSD post-hoc test, and the Bonferroni test, all at a 5% significance level. For each group, a paired samples test was applied to compare the DC of the immediate and 24 h samples. Results: The highest FS value was found for the Prevision Temp material, while the Charm Temp material showed the lowest FS, with no statistically significant difference between the mean values of the groups at 24 h; while there were significant differences at 7d and 14 d of storage. However, within each group, the aging had no significant impact on the FS, except for an increase in the FS of the B&E CROWN group after 14 d. Prevision Temp also had the highest mean DC value. At each time interval, significant differences were recorded. Moreover, within each group of material, aging significantly increased the DC, except for the Primma Art. Conclusion: Bis-acryl composite resin materials exhibited higher flexural strength compared to traditional methyl methacrylate resin during the 14 d investigation period. Aging in artificial saliva did not significantly affect the mechanical performance of the tested materials. Materials with higher DC values showed greater flexural strength; where the Prevision Temp showed higher FS and DC values than the other tested materials. KEYWORDS Aging; Artificial saliva; Degree of conversion; Flexural strength; Temporary crown material.

This study aimed to evaluate potential impacts of calcium oxide nanoparticles (CaO-NPs) at different dosages on predentin thickness, number of blood vessels, periodontal ligament thickness, and blood glucose level of Wistar rats. Twelve rats were randomly gathered into four groups, untreated (control) and CaO-NP-treated groups at three concentrations (25, 50, and 100 mg/kg of the body weight) over a period of 60 days. Histological investigation was performed on twenty-four lower incisor teeth extracted from all the tested groups under a light microscope, and an automatic Fujifilm was used to measure the blood glucose level. The results showed that regular nanoparticle treatment significantly increased predentin and periodontal ligament thicknesses, a gradual decrease in vascularization in the pulp tissue, and an increase in the blood glucose level as the dosages of nanoparticles administered to the rats increased. Administration of the CaO-NPs at low dosage (25 mg/kg) could be beneficial for the growth and integrity of teeth and dentinal tissues in rats.