Additive manufacturing (AM) is a broad definition of various techniques to produce layer-by-layer objects made of different materials. In this paper, a comprehensive review of laser-based technologies for polymers, including powder bed fusion processes [e.g. selective laser sintering (SLS)] and vat photopolymerisation [e.g. stereolithography (SLA)], is presented, where both the techniques employ a laser source to either melt or cure a raw polymeric material. The aim of the review is twofold: (1) to present the principal theoretical models adopted in the literature to simulate the complex physical phenomena involved in the transformation of the raw material into AM objects and (2) to discuss the influence of process parameters on the physical final properties of the printed objects and in turn on their mechanical performance. The models being presented simulate: the thermal problem along with the thermally activated bonding through sintering of the polymeric powder in SLS; the binding induced by the curing mechanisms of light-induced polymerisation of the liquid material in SLA. Key physical variables in AM objects, such as porosity and degree of cure in SLS and SLA respectively, are discussed in relation to the manufacturing process parameters, as well as to the mechanical resistance and deformability of the objects themselves. Graphic

This paper presents a study on the tensile properties of Alumide and polyamide PA2200 standard samples produced by Additive manufacturing (AM) based on selective laser sintering (SLS). Because of the orthogonal trajectories of the laser beam during exposure, different orientations of the samples may lead to different mechanical properties. In order to reveal this process issue, four orientations of the samples in building envelope were investigated. For data reliability, all the other process parameters were constant for each material and every orientation. The tensile tests highlight small differences in elastic properties of the two materials, while significant differences in strength properties and energy absorption were observed. Nevertheless, Young modulus indicates high stiffness of the Alumide comparing to PA2200 samples. The stereo microscopy reveals a brittle fracture site for Alumide and a ductile fracture with longitudinal splitting zones for PA2200. From the orientation point of view, similar properties of samples oriented at 0 and 90 degrees for all investigated mechanical properties were observed. However, tensile strength was less influenced by the sample orientations.