This study examines the effects of stick-out, welding current, welding speed, and voltage on the mechanical characteristics and microstructure of MIG welding on SUS 304 stainless steel and S20C steel. The Taguchi method was used to maximize the experiment’s outcomes. Fine columnar dendrites formed at fusion sites, and δ-ferrite phases with dark lines and shapes accumulated between the fusion line and the austenite phases. A welding current of 110 A, voltage of 15 V, welding speed of 500 mm/min, and stick-out of 12 mm were the optimal settings for the ultimate tensile strength (UTS). The UTS value confirmation was 469.4 MPa, which agrees with the estimated value determined using the Taguchi technique. The tensile test revealed that welding current had a far greater impact on mechanical qualities than welding voltage, speed, and stick-out distance. The ideal welding parameters for flexural strength were as follows: stick-out of 12 mm, arc voltage of 15 V, welding speed of 450 mm/min, and welding current of 110 amp. The Taguchi method is useful, as evidenced by the validation of the flexure strength of 1937.45 MPa, which is much greater than the other samples. The impact of the thermal annealing process on the mechanical characteristics of the dissimilar weld joints could be the subject of future research. The investigation results may offer more insightful information about the dissimilar welding field.

This study looks at how welding intensity, speed, voltage, and stick-out affect the structural and mechanical characteristics of metal inert gas (MIG) welding on SUS 201 stainless steel and C20 steel. The Taguchi method is used to optimize the study’s experiment findings. The results show that the welding current has a more significant effect on the tensile test than the welding voltage, stick-out, and welding speed. Welding voltage has the lowest influence. In addition to the base metals’ ferrite, pearlite, and austenite phases, the weld bead area contains martensite and bainite microstructures. The optimal parameters for the ultimate tensile strength (UTS), yield strength, and elongation values are a 110 amp welding current, 15 V of voltage, a 500 mm.min⁻¹ welding speed, and a 10 mm stick-out. The confirmed UTS, yield strength, and elongation values are 452.78 MPa, 374.65 MPa, and 38.55%, respectively, comparable with the expected value derived using the Taguchi method. In the flexural test, the welding current is the most critical element affecting flexural strength. A welding current of 110 amp, an arc voltage of 15 V, a welding speed of 500 mm.min⁻¹, and a stick-out of 12 mm are the ideal values for flexural strength. The flexural strength, confirmed at 1756.78 MPa, is more than that of the other samples. The study’s conclusions can offer more details regarding the dissimilar welding industry.

Orbital TIG welding is widely applied to weld pipes to pipes in many fields, such as food, chemicals, oil, gas, and transportation. Optimizing welding parameters such as voltage, current, and travel speed is critical to achieve a good-quality weld. This study investigated the impacts of orbital welding parameters and filler wire diameters on the tensile strength of 304 stainless steel pipes. The 304 stainless steel pipe has an outer diameter of 76 mm and a thickness of 2 mm. Filler wire is used with the workpiece, and is available in three diameters of 0.8 mm, 1 mm, and 1.2 mm, wire feed speed from 3.8 mm/s to 5.6 mm/s, current from 90 A to 110 A, and travel speed fixed at 5.5 mm/s. The highest tensile strength of 562 MPa was achieved with heat input of 0.32 kJ/mm and wire feed speed of 3.8 mm/s. In addition, the best parameters via the Taguchi method were found. The parameters’ influence trends on the weld quality were also revealed.

The high-pressure die-casting (HPDC) process involves injecting molten light metal into a steel mold under high pressure, resulting in parts with excellent surface quality and precise dimensions. However, this process subjects the mold to thermal fatigue and mechanical stress, which can lead to damage over time. This study investigated the wear characteristics of two types of inserts made from different steel materials, SKD61 steel and FDAC steel, under HPDC conditions. A thorough approach that combined computer simulations, experiments, and 3D scanning was employed to analyze wear patterns and dimensional changes after up to 300 casting cycles. The results indicate that the SKD61 steel outperformed the FDAC steel in terms of wear resistance and dimensional stability. The maximum deposition values of the SKD61 mold were only 0.009 mm, which was only 25% compared to the FDAC mold, indicating a significantly higher wear resistance. These findings are crucial for selecting and enhancing insert materials in HPDC, ultimately leading to higher-quality and more efficient casting.

Taguchi and post-heat treatment methods have been used in this study to optimize the metal inert gas (MIG) welding joints between SUS304 austenite stainless steel and plain carbon SS400 steel using AWS ER 308L filler wire. The dissimilar welding joints’ microstructure and tensile strength have been examined. The findings show that the fast cooling of the weld joint and the ferrite-forming element of the filler wire cause the dendrites’ δ-ferrite phase to emerge on both the weld bead and the heat-affected zone (HAZ) of the SUS304 side. The stickout parameter has the largest impact on the ultimate tensile strength (UTS), next to the welding speed, welding voltage, and welding current, due to the strong impact of the heat distribution. The optimal welding parameters are a welding current of 105 A, a welding voltage of 14.5 V, a stickout of 12 mm, and a welding speed of 420 mm/min, producing the UTS value of 445.3 MPa, which is close to the predicted value of 469.2 ± 53.6 MPa. Post-heat treatment with an annealing temperature that is lower than 700 °C could improve the optimized weld joints’ strength by up to 5%. The findings may provide a more realistic understanding of the dissimilar welding technology.