This study investigated the influence of parameters such as pH condition, polyelectrolyte concentration, polymer ratio, and order of addition of the commercial polyelectrolytes chitosan and iota-carrageenan (ι-carrageenan) on the formation of polymeric nanoparticles in suspension (coacervates). A preliminary purification step of the polymers was essential for obtaining stable nanoparticles with small sizes as impurities, particularly metal ions that interfere with complexation, are removed by dialysis. Microparticles (13.5 μm in dry diameter) are obtained when aliquots of chitosan solution are poured into the ι-carrageenan solution. In general, an excess of chitosan results in the formation of agglomerated particles. The addition of an aliquot of ι-carrageenan solution (30 mL at 0.6 mg/mL and pH 4.0) to the chitosan solution (6.0 mL at 0.3 mg/mL and pH 4.0) leads to dispersed nanoparticles with a hydrodynamic radius of 278 ± 5 nm, a zeta potential of −31 ± 3 mV, and an average dry diameter of 45 ± 11 nm. The hydrodynamic radius increases as the pH rises. The partial deprotonation of ι-carrageenan chains enhances the interaction with water molecules, causing the particles to swell. These findings contribute to the fundamental understanding of polyelectrolyte complexation processes in aqueous suspension and provide insights for developing stable nanomaterials for potential practical applications.

This study presents the development of fibers with favorable properties for biodegradable wound dressings made from the Ecovio^® (EC) polymer blend, composed of poly(lactic acid) (PLA) and poly(butylene adipate-co-terephthalate) (PBAT), incorporated with tea tree essential oil (TTE). TTE presented antimicrobial activity against Pseudomonas aeruginosa and Staphylococcus aureus, achieving minimal inhibitory concentrations (MIC) of 15 and 7.5 mg/mL, respectively. The TTE was mixed with EC in a binary chloroform and formic acid (85/15 v/v) mixture. The EC/TTE fibers were characterized by differential scanning calorimetry (DSC), Fourier-transform infrared with attenuated total reflectance (FTIR-ATR), and X-ray photoelectron spectroscopy (XPS), confirming the TTE in the fibers. The tests showed that TTE (0.5, 1.0, or 1.5 mL) improved the polymer blend’s electrospinnability, leading to bead-free, homogenous, and smaller fiber diameters. TTE (1.5 mL or 75 w% concerning the EC) leads to homogeneous fibers with an average diameter of 278 ± 59 nm. TTE (75 w%) increased the wettability of the EC fibers from 120 ± 2° to 69 ± 1°. Preliminary bacterial adhesion and proliferation assays demonstrated that the EC/TTE fibers have anti-adhesive activity and demonstrate greater toxicity, which seems more toxic against P. aeruginosa than S. aureus after 24 h of incubation. Fluorescence and coagulation kinetics tests performed with human blood indicated that the EC/TTE fibers accelerate blood coagulation. The EC/TTE fibers exhibit promising chemical and biological properties (in vitro) for developing wound dressings.

Fungi (Neolentinus lepideus, Nl, and Trametes versicolor, Tv) impart wood rot, leading to economic and environmental issues. To overcome this issue, toxic chemicals are commonly employed for wood preservation, impacting the environment and human health. Surface coatings based on antimicrobial chitosan (CS) of high molar mass (145 × 10⁵ Da) were tested as wood preservation agents using an innovative strategy involving ultra-pressurizing CS solutions to deposit organic coatings on wood samples. Before coating deposition, the antifungal activity of CS in diluted acetic acid (AcOOH) solutions was evaluated against the rot fungi models Neolentinus lepideus (Nl) and Trametes versicolor (Tv). CS effectively inhibited fungal growth, particularly in solutions with concentrations equal to or higher than 0.125 mg/mL. Wood samples (Eucalyptus sp. and Pinus sp.) were then coated with CS under ultra-pressurization at 70 bar. The polymeric coating deposition on wood was confirmed through X-ray photoelectron spectroscopy (XPS), energy dispersive X-ray spectroscopy (EDS), scanning electron microscopy (SEM) images, and water contact angle measurements. Infrared spectroscopy (FTIR) spectra of the uncoated and coated samples suggested that CS does not penetrate the bulk of the wood samples due to its high molar mass but penetrates in the surface pores, leading to its impregnation in wood samples. Coated and uncoated wood samples were exposed to fungi (Tv and Nl) for 12 weeks. In vivo testing revealed that Tv and Nl fungi did not grow on wood samples coated with CS, whereas the fungi proliferated on uncoated samples. CS of high molar mass has film-forming properties, leading to a thin hydrophobic film on the wood surface (water contact angle of 118°). This effect is mainly attributed to the high molar mass of CS and the hydrogen bonding interactions established between CS chains and cellulose. This hydrophobic film prevents water interaction, resulting in a stable coating with insignificant leaching of CS after the stability test. The CS coating can offer a sustainable strategy to prevent wood degradation, overcoming the disadvantages of toxic chemicals often used as wood preservative agents.

This study presents, for the first time, the development of fibers with favorable properties for biodegradable wound dressings made from the Ecovio® (EC) polymer blend, composed of poly(lactic acid) (PLA) and poly(butylene adipate-co-terephthalate) (PBAT), incorporated with tea tree essential oil (TTE). TTE presented antimicrobial activity against Pseudomonas aeruginosa and Staphylococcus aureus, achieving minimal inhibitory concentrations of 15 and 7.5 mg/mL, respectively. The TTE was mixed with EC in a binary chloroform and formic acid (85/15 v/v) mixture, leading to homogeneous and wettable fibers by electrospinning. The EC/TTE fibers were characterized confirming the TTE in the fibers. The tests showed that TTE (0.5, 1.0 or 1.5 mL) improved the polymer blend electrospinnability. TTE (1.5 mL or 75 w% concerning the EC) lead to homogeneous fibers with an average diameter of 278 nm. TTE (75 w%) increased the wettability of the EC fibers from 120±2° to 69±1°. Preliminary bacterial adhesion and proliferation assays demonstrated that the EC/TTE fibers have anti-adhesive activity e seems to be more toxic against P. aeruginosa compared to S. aureus after 24 hours of incubation. Compatibility tests with human blood indicated that the EC/TTE fibers accelerate blood coagulation. The EC/TTE fibers exhibit promising chemical and biological properties (in vitro) for the development of wound dressings.