Adenovirus-mediated gene therapy is a promising tool in bone regenerative medicine. In this work, gene-activated matrices (GAMs) composed of (1) polylactide granules (PLA), which serve as a depot for genetic constructs or matrices for cell attachment, (2) a PRP-based fibrin clot, which is a source of growth factors and a binding gel, and (3) a BMP2 gene providing osteoinductive properties were studied. The study aims to compare the effectiveness of in vivo and ex vivo gene therapy based on adenoviral constructs with the BMP2 gene, PLA particles, and a fibrin clot for bone defect healing. GAMs with Ad-BMP2 and MSC(Ad-BMP2) show osteoinductive properties both in vitro and in vivo. However, MSCs incubated with GAMs containing transduced cells showed a more significant increase in osteopontin gene expression, protein production, Alpl activity, and matrix mineralization. Implantation of the studied matrices into critical-size calvarial defects after 56 days promotes the formation of young bone. The efficiency of neoosteogenesis and the volume fraction of newly formed bone tissue are higher with PLA/PRP-MSC(Ad-BMP2) implantation (33%) than PLA/PRP-Ad-BMP2 (28%). Thus, ex vivo adenoviral gene therapy with the BMP2 gene has proven to be a more effective approach than the in vivo delivery of gene constructs for bone regeneration.

Dehydroepiandrosterone (DHEA), a precursor of steroid sex hormones, is synthesized by steroid 17-alpha-hydroxylase/17,20-lyase (CYP17A1) with the participation of microsomal cytochrome b5 (CYB5A) and cytochrome P450 reductase (CPR), followed by sulfation by two cytosolic sulfotransferases, SULT1E1 and SULT2A1, for storage and transport to tissues in which its synthesis is not available. The involvement of CYP17A1 and SULTs in these successive reactions led us to consider the possible interaction of SULTs with DHEA-producing CYP17A1 and its redox partners. Text mining analysis, protein–protein network analysis, and gene co-expression analysis were performed to determine the relationships between SULTs and microsomal CYP isoforms. For the first time, using surface plasmon resonance, we detected interactions between CYP17A1 and SULT2A1 or SULT1E1. SULTs also interacted with CYB5A and CPR. The interaction parameters of SULT2A1/CYP17A1 and SULT2A1/CYB5A complexes seemed to be modulated by 3′-phosphoadenosine-5′-phosphosulfate (PAPS). Affinity purification, combined with mass spectrometry (AP-MS), allowed us to identify a spectrum of SULT1E1 potential protein partners, including CYB5A. We showed that the enzymatic activity of SULTs increased in the presence of only CYP17A1 or CYP17A1 and CYB5A mixture. The structures of CYP17A1/SULT1E1 and CYB5A/SULT1E1 complexes were predicted. Our data provide novel fundamental information about the organization of microsomal CYP-dependent macromolecular complexes.

Background/Objectives: The replenishment of bone deficiency remains a challenging task in clinical practice. The use of gene-activated matrices (GAMs) impregnated with genetic constructs may be an innovative approach to solving this problem. The aim of this work is to develop collagen-based matrices with the addition of platelet-rich plasma, carrying polyplexes with the BMP2 gene, to study their biocompatibility and osteogenic potential in vitro and in vivo. Methods: The cytocompatibility of the materials during incubation with adipose-derived stem cells (ADSCs) was studied using the MTT test and fluorescent microscopy. Biocompatibility was assessed during intramuscular implantation, followed by histological analysis. Osteogenic differentiation was determined by the expressions of Alpl and Bglap using real-time PCR and extracellular matrix (ECM) mineralization by alizarin red staining. The efficiency of bone regeneration was studied using micro-CT and analysis of histological sections stained according to Masson. Results: After the incubation of ADSCs with GAS, significant increases in the expressions of the Alpl and Bglap genes by 3 ± 0.1 and 9.9 ± 0.6 times, relative to the control, as well as mineralization of the ECM, were observed. The volume of newly formed bone was 37.2 ± 6.2% after implantation of GAS, 20.9 ± 1.2%—non-activated Col/PRP, and 2.6 ± 1.5% in an empty defect. Conclusions: The use of Col/PRP-based matrices is an effective method for delivering of the osteoinductor gene to the site of bone tissue damage. The highest degree of healing was observed after the implantation of Col/PRP-TF/pBMP2 into the critical size defect compared to the other groups.

In regenerative medicine, orthobiologics, particularly platelet-rich plasma (PRP), are widely used due to their ability to enhance natural tissue repair mechanisms. PRP contains a concentrated pool of growth factors and cytokines that enhance regeneration while also acting as a biomimetic scaffold, thereby optimizing the microenvironment for tissue healing. In bone tissue engineering, PRP is commonly combined with synthetic or natural biomaterials, as its fibrin matrix alone lacks sufficient mechanical stability. However, even such composite systems frequently exhibit limited osteoinductive capacity, necessitating further supplementation with bioactive components. This review evaluates the regenerative potential of PRP in bone defect healing when combined with osteoinductive agents in preclinical in vivo models. We present compelling experimental evidence supporting the efficacy of this combined therapeutic approach.

The use of 3D-printed gene-activated bone grafts represents a highly promising approach in the fields of dentistry and orthopedics. Bioresorbable poly-lactic-co-glycolic acid (PLGA) scaffolds, infused with adenoviral constructs that carry osteoinductive factor genes, may provide an effective alternative to existing bone grafts for the reconstruction of extensive bone defects. This study aims to develop and investigate the properties of 3D scaffolds composed of PLGA and adenoviral constructs carrying the BMP2 gene (Ad-BMP2), both in vitro and in vivo. The elastic modulus of the disk-shaped PLGA scaffolds created using a specialized 3D printer was determined by compressive testing in both axial and radial directions. In vitro cytocompatibility was assessed using adipose-derived stem cells (ADSCs). The ability of Ad-BMP2 to transduce cells was evaluated. The osteoinductive and biocompatible properties of the scaffolds were also assessed in vivo. The Young’s modulus of the 3D-printed PLGA scaffolds exhibited comparable values in both axial and radial compression directions, measuring 3.4 ± 0.7 MPa for axial and 3.17 ± 1.4 MPa for radial compression. The scaffolds promoted cell adhesion and had no cytotoxic effect on ADSCs. Ad-BMP2 successfully transduced the cells and induced osteogenic differentiation in vitro. In vivo studies demonstrated that the 3D-printed PLGA scaffolds had osteoinductive properties, promoting bone formation within the scaffold filaments as well as at the center of a critical calvarial bone defect.

Objective. Study of cytocompatibility of hydroxyapatite coating for titanium implants applied by high-frequency magnetron sputtering at low pressures in an inert gas atmosphere. Materials and methods. Hydroxyapatite was deposited on titanium substrates using the HF magnetron sputtering method. The cytocompatibility of the materials was assessed by incubating with multipotent mesenchymal stromal cells (MSCs) using the MTT assay. Adhesion properties were studied by staining cells with fluorescent dyes and using scanning electron microscopy. Results. The studied titanium materials possess high cytocompatibility. The number of living cells on the 7th day was 100.0±5.6% and 108.5±8.7% for materials with and without coating, respectively. Furthermore, coating titanium substrates with hydroxyapatite resulted in a statistically significant 1.7±0.4-fold increase in the number of adhered MSCs compared to uncoated materials. Conclusion. The hydroxyapatite coating applied using HF magnetron sputtering significantly improves cell adhesion to titanium materials. Thus, the obtained results provide a basis for the development of new implants with functionalized surfaces.