In this study, near-liquidus squeeze casting AZ91D alloy was used to prepare differential support, and the microstructure and mechanical behavior under different applied pressure were investigated. Under the preset temperature, speed, and other process parameters, the effect of applied pressure on the microstructure and properties of formed parts was analyzed, and relevant mechanism was also discussed. The results showed that the ultimate tensile strength (UTS) and elongation (EL) of differential support can be improved by controlling real-time precision of the forming pressure. The dislocation density in the primary phase increased obviously with the pressure increasing from 80 MPa to 170 MPa, and even tangles appeared. When the applied pressure increased from 80 MPa to 140 MPa, the α-Mg grains were gradually refined, and the microstructure changed from rosette to globular shape. With increasing the applied pressure to 170 MPa, the grain could not be further refined. Similarly, its UTS and EL gradually increased with the applied pressure increasing from 80 MPa to 140 MPa. With increasing to 170 MPa, the UTS tended to be constant, but the EL gradually decreased. In other words, the UTS (229.2 MPa) and EL (3.43%) of the alloy reached the maximum when the applied pressure was 140 MPa, and the comprehensive mechanical properties were the best.

The inefficiency of grain refinement processes has traditionally been attributed to the limited utilization of heterogeneous nucleation particles within master alloy systems, resulting in the formation of abundant inactive particles. This study aims to investigate the alternative influences of particles by incorporating external micrometer-sized TiB₂ particles into the grain refinement process. Through a series of experiments, the refinement efficiency, grain refinement mechanism, and resultant microstructure of TiB₂ particle-induced grain refinement specimens are comprehensively examined using various microscopy and analytical techniques, including polarization microscopy (OM), scanning electron microscopy (SEM), differential scanning calorimetry (DSC), and transmission electron microscopy (TEM). Our findings demonstrate a direct correlation between increased levels of TiB₂ particles and enhanced grain refinement efficiency. Moreover, the microstructure analysis reveals the distribution of TiB₂ particles along grain boundaries, forming a coating due to self-assembly phenomena, while regions with a lower particle content may exhibit irregular grain structures. DSC analysis further confirms reduced undercooling, indicating the occurrence of heterogeneous nucleation events. However, TEM observations suggest that heterogeneous nucleation is not significantly influenced by the growth restriction factor attributed to TiAl₃ 2DC compounds. The grain refinement mechanism involving TiB₂ particles is elucidated to entail both heterogeneous nucleation and physical growth restriction effects. Specifically, a reduction in average grain size is attributed not only to heterogeneous nucleation but also to the physical growth restriction effect facilitated by the TiB₂ particle coating. This study offers insights into leveraging particles that do not participate in heterogeneous nucleation within master alloy-based grain refinement systems.

The refining performance of Al-Ti-C master alloys is substantially compromised by the inferior wettability between graphite and molten aluminum. In this paper, the Al-5Ti-0.25C master alloy was successfully prepared by reacting Ti machining chips, graphite, and molten aluminum. In order to determine a simple method of improving the wettability, the optimal preparation process and phase transformation of the Al-5Ti-0.25C master alloy were investigated using an optical microscope, X-ray diffractometer, and scanning electron microscope equipped with an energy dispersive spectrometer. The results show that the feeding method using a prefabricated block made from Ti chips, Al chips, and graphite effectively improves the wettability between graphite and molten aluminum and increases the recovery rate of graphite. When the reaction temperature is low (1223 K), the agglomeration of TiAl₃ is caused. When the reaction temperature is high (1373 K), the morphology of TiAl₃ changes from block-like to needle-like and increases its size. Further, a short reaction time (30 min) results in the incomplete dissolution of the Ti chips, while a long reaction time (90 min) causes the TiAl₃ to transform into needle-like morphologies. The microstructural observation of undissolved Ti chips shows that TiAl₃ and TiC are formed around it, which proves the transformation of Ti chips to TiAl₃ and TiC. In addition, the enrichment of TiC and Al₄C₃ was observed in the vicinity of TiAl₃, and a reaction model for the formation of TiC from the reaction of Al₄C₃ and TiAl₃ was presented.