Late transition metal catalysts represent a significant class of olefin polymerization catalysts that have played an essential role in advancing the polyolefin industry owing to their highly tunable ligands and low oxophilicity. A key feature for the design of late transition metal catalysts lies in the steric bulk of the o-aryl substituents. Bulky 8-arylnaphthylamines have emerged as a promising aniline candidate for conducting high-performance catalysts by introducing axially steric hindrance around the metal center. This review focuses on late transition metal (Ni, Pd, Fe) catalysts derived from 8-arylnaphthylamines, surveying their synthesis, structural features, and catalytic applications in olefin (co)polymerizations. Additionally, the relationship between catalyst structure and catalytic performance is discussed, highlighting how these unique ligand systems influence polymerization activity, molecular weight, and polymer branching.

The development of earth-abundant nickel-based catalysts is currently one of the greatest challenges for the straightforward synthesis of functionalized polyolefins. With environmental protection concerns, controllable copolymerizations of ethylene with biosourced comonomers derived from castor oil, such as methyl 10-undecenoate (U-COOMe), 10-undecen-1-ol (U-OH), or 10-undecenyl bromide (U-Br), were realized using α-diimine nickel catalyst (Ni-DBB) with dibenzobarrelene backbone. Catalyst Ni-DBB was highly tolerant toward polar comonomers, and functional polyethylenes were successfully prepared. The influences of the polar group, temperature, and comonomer concentration were studied in detail. Catalyst Ni-DBB was able to catalyze the copolymerization of ethylene with U-OH to afford high-molecular-weight (~180 kg/mol) functional polyethylene in a controlled fashion. NMR analysis showed that the produced functional polyethylenes were highly branched and had broad melting peaks ranging from 0 to 30 °C. Water contact angle (WCA) measurements showed that the surface of the obtained hydroxyl-functionalized polyethylene changed from hydrophobic to hydrophilic with the introduction of the comonomer U-OH.