The incorporation of defects, such as vacancies, into functional materials could substantially tailor their intrinsic properties. Progress in vacancy chemistry has enabled advances in many technological applications, but creating new type of vacancies in existing material system remains a big challenge. We show here that ionized nitrogen plasma can break bonds of iron-carbon-nitrogen-nickel units in nickel-iron Prussian blue analogues, forming unconventional carbon-nitrogen vacancies. We study oxygen evolution reaction on the carbon-nitrogen vacancy-mediated Prussian blue analogues, which exhibit a low overpotential of 283 millivolts at 10 milliamperes per square centimeter in alkali, far exceeding that of original Prussian blue analogues and previously reported oxygen evolution catalysts with vacancies. We ascribe this enhancement to the in-situ generated nickel-iron oxy(hydroxide) active layer during oxygen evolution reaction, where the Fe leaching was significantly suppressed by the unconventional carbon-nitrogen vacancies. This work opens up opportunities for producing vacancy defects in nanomaterials for broad applications.

Sustainable structural materials with light weight, great thermal dimensional stability, and superb mechanical properties are vitally important for engineering application, but the intrinsic conflict among some material properties (e.g., strength and toughness) makes it challenging to realize these performance indexes at the same time under wide service conditions. Here, we report a robust and feasible strategy to process cellulose nanofiber (CNF) into a high-performance sustainable bulk structural material with low density, excellent strength and toughness, and great thermal dimensional stability. The obtained cellulose nanofiber plate (CNFP) has high specific strength [~198 MPa/(Mg m⁻³)], high specific impact toughness [~67 kJ m⁻²/(Mg m⁻³)], and low thermal expansion coefficient (<5 × 10⁻⁶ K⁻¹), which shows distinct and superior properties to typical polymers, metals, and ceramics, making it a low-cost, high-performance, and environmental-friendly alternative for engineering requirement, especially for aerospace applications.

Woods provide bioinspiration for engineering materials due to their superior mechanical performance. We demonstrate a novel strategy for large-scale fabrication of a family of bioinspired polymeric woods with similar polyphenol matrix materials, wood-like cellular microstructures, and outstanding comprehensive performance by a self-assembly and thermocuring process of traditional resins. In contrast to natural woods, polymeric woods demonstrate comparable mechanical properties (a compressive yield strength of up to 45 MPa), preferable corrosion resistance to acid with no decrease in mechanical properties, and much better thermal insulation (as low as ~21 mW m⁻¹ K⁻¹) and fire retardancy. These bioinspired polymeric woods even stand out from other engineering materials such as cellular ceramic materials and aerogel-like materials in terms of specific strength and thermal insulation properties. The present strategy provides a new possibility for mass production of a series of high-performance biomimetic engineering materials with hierarchical cellular microstructures and remarkable multifunctionality.